Characterization of Al-Si cast alloys reinforced by(Al2 O3 )NANO-particles /
Warda Aboualhassan Mohammed Marzok
Characterization of Al-Si cast alloys reinforced by(Al2 O3 )NANO-particles / الخصائص المميزة لسبيكة الالومنيوم-سيليكون المدعمة(المقواه)بحبيبات اكسيد الالومنيوم النانوية Warda Aboualhassan Mohammed Marzok ; Supervised Abdelhamid A. Hussein , Iman S. Elmahallawi , Tamer S. Mahmoud - Cairo : Warda Aboualhassan Mohammed Marzok , 2009 - 73P. : charts , facsimiles ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Metallurgical Engineering
In the present study A356 aluminum alloy was reinforced with Al2O3 particles using rheocasting(semi-solid casting) route.This route exhibits many advantages when compared with the traditional liquid metallurgy processing techniques such as stir casting or vortex method
A356 aluminumalloy Metal matrix Composite Particles
Characterization of Al-Si cast alloys reinforced by(Al2 O3 )NANO-particles / الخصائص المميزة لسبيكة الالومنيوم-سيليكون المدعمة(المقواه)بحبيبات اكسيد الالومنيوم النانوية Warda Aboualhassan Mohammed Marzok ; Supervised Abdelhamid A. Hussein , Iman S. Elmahallawi , Tamer S. Mahmoud - Cairo : Warda Aboualhassan Mohammed Marzok , 2009 - 73P. : charts , facsimiles ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Metallurgical Engineering
In the present study A356 aluminum alloy was reinforced with Al2O3 particles using rheocasting(semi-solid casting) route.This route exhibits many advantages when compared with the traditional liquid metallurgy processing techniques such as stir casting or vortex method
A356 aluminumalloy Metal matrix Composite Particles