Influence Of Diode Laser Irradiation On Shear Bond Strength Of Activa™ And Composite Resin Restorations In Primary Molars / An In Vitro Study /
Sally Ahmed Kotb,
Influence Of Diode Laser Irradiation On Shear Bond Strength Of Activa™ And Composite Resin Restorations In Primary Molars / An In Vitro Study / دراسة تأثير اشعاع الليزر الدايود على القوة القصية في حشوات (Activa) وحشوات الكومبوزت للأسنان اللبنية : دراسة معملية / by Sally Ahmed Kotb ; Supervisors . Dr. Randa Youssef Abd Al Gawad, Dr. Shaimaa Mohamed Sabry - 85 pages : illustrations ; 25 cm. + CD.
Thesis (M.Sc.)-Cairo University, 2022.
Bibliography: pages 78-84.
The aim of this study is to evaluate the influence of diode laser irradiation on the bond strength
of two esthetic restorative materials; Activa bioactive restoration and composite resin.
Methodology: 104 primary molars were collected and divided into two main groups (n=52) (Laser and
No laser). Teeth were mounted in acrylic molds and prepared to expose enamel and dentin surfaces.
Samples of each group were randomly distributed into 4 subgroups: Activa + enamel, Activa + dentin,
composite + enamel and composite + dentin. Enamel samples were etched,while universal adhesive
was used for Activa and composite samples in dentin, .Diode laser irradiation (980nm wavelength, 1W
power, continuous mode) was applied after adhesive application and before polymerization. After
thermocycling for 500 cycle, microshear bond was measured using universal testing machine and
values were obtained in MPs. Statistical analysis was done using three ways ANOVA.
Results: Mean bond strength of enamel samples were significantly higher than dentin samples
(p<0.05).In Activa bioactive restoration samples, diode laser irradiation significantly reduced
microshear bond strength in enamel and dentin. Irradiation with diode laser did not significantly
improve the mean microshear bond strength in enamel and dentin composite samples.
Conclusion: Diode laser irradiation did not improve bond strength of composite restorations when
applied before adhesive polymerization of primary teeth and had negative effect on bond strength of
Activa bioactive restorations. الحشوات اللتجميلية الحديثة اصبحت محل اهتمام و غاية للاطفال في العالم الحديث .يتطلب الحشوات التجميلية أنظمة لاصقة قوية ؛أحد الاهتمامات الرئيسية في استخدام الأنظمة اللاصقة هو الحصول على رابطة كافية بين الحشوات وأنسجة الأسنان. يعد تحضير أنسجة الأسنان قبل عمل الحشوات خطوة مهمة في بروتوكول اللصق الذي يحدد نجاح العلاج. يعتبر الارتباط بالعاج أكثر صعوبة من الارتباط بالمينا بسبب النمط الأنبوبي للعاج ، وارتفاع محتوى الماء ، ووجود طبقة اللطاخة ، والتغيرات الفيزيولوجية المرضية مثل وجود عاج شديد التمعدن ومتصلب.تهدف هذه الدراسة إلى تقييم تأثير استخدام إشعاع ليزر الدايود على قوة الترابط بين مادتين ترميميتين تجميليتين ؛Activa والكومبوزت.
تم جمع مائة وأربعة أضراس لبنية وتقسيمها إلى مجموعتين رئيسيتين (ليزر وبدون ليزر). تم تركيب الأسنان في قوالب أكريليك وتجهيزها لكشف أسطح المينا وعاج الأسنان. تم توزيع عينات كل مجموعة عشوائيًا إلى 4 مجموعات فرعية: المجموعة الفرعية 1: حشو Activa المرتبط بالمينا ، المجموعة الفرعية 2: حشوActiva المرتبط بالعاج ، المجموعة الفرعية 3: حشو كومبوزت مرتبط بركيزة المينا والمجموعة الفرعية 4: حشو كومبوزت مرتبط بركيزة العاج .تم استخدام المادة اللاصقة العامة لعينات الكومبوزت و Activa في العاج ، بينما تم حفر عينات المينا بشكل انتقائي. تم تطبيق إشعاع ليزر الدايود (الطول الموجي 980 نانومتر ، الطاقة 1 واط ، الوضع المستمر) بعد تطبيق المادة اللاصقة وقبل البلمرة. بعد التدوير الحراري لمدة 500 دورة ، تم إجراء اختبار السندات المصغرة باستخدام آلة اختبار عامة. تم إجراء التحليل الإحصائي باستخدام ثلاث طرق ANOVA.
كان متوسط قوة الرابطة لعينات المينا أعلى بكثير من عينات العاج (P <0.05). لم يحسن التشعيع بليزر الدايود بشكل كبير متوسط قوة الرابطة الدقيقة في عينات المينا وعاج الأسنان. في عينات Activa ، قلل تشعيع ليزر الدايود بشكل كبير من قوة الرابطة الدقيقة في المينا والعاج. يمكن الاستنتاج أن تشعيع ليزر الدايود لم يحسن قوة الترابط لحشوات الكومبوزت عند تطبيقها قبل بلمرة المادة اللاصقة وكان لها تأثير سلبي على قوة الرابطة لترميمات Activa.
Text in English and abstract in Arabic & English.
Pediatric Dentistry
Bond strength Diode laser Primary molars Activa Bioactive Composite resin
617.645
Influence Of Diode Laser Irradiation On Shear Bond Strength Of Activa™ And Composite Resin Restorations In Primary Molars / An In Vitro Study / دراسة تأثير اشعاع الليزر الدايود على القوة القصية في حشوات (Activa) وحشوات الكومبوزت للأسنان اللبنية : دراسة معملية / by Sally Ahmed Kotb ; Supervisors . Dr. Randa Youssef Abd Al Gawad, Dr. Shaimaa Mohamed Sabry - 85 pages : illustrations ; 25 cm. + CD.
Thesis (M.Sc.)-Cairo University, 2022.
Bibliography: pages 78-84.
The aim of this study is to evaluate the influence of diode laser irradiation on the bond strength
of two esthetic restorative materials; Activa bioactive restoration and composite resin.
Methodology: 104 primary molars were collected and divided into two main groups (n=52) (Laser and
No laser). Teeth were mounted in acrylic molds and prepared to expose enamel and dentin surfaces.
Samples of each group were randomly distributed into 4 subgroups: Activa + enamel, Activa + dentin,
composite + enamel and composite + dentin. Enamel samples were etched,while universal adhesive
was used for Activa and composite samples in dentin, .Diode laser irradiation (980nm wavelength, 1W
power, continuous mode) was applied after adhesive application and before polymerization. After
thermocycling for 500 cycle, microshear bond was measured using universal testing machine and
values were obtained in MPs. Statistical analysis was done using three ways ANOVA.
Results: Mean bond strength of enamel samples were significantly higher than dentin samples
(p<0.05).In Activa bioactive restoration samples, diode laser irradiation significantly reduced
microshear bond strength in enamel and dentin. Irradiation with diode laser did not significantly
improve the mean microshear bond strength in enamel and dentin composite samples.
Conclusion: Diode laser irradiation did not improve bond strength of composite restorations when
applied before adhesive polymerization of primary teeth and had negative effect on bond strength of
Activa bioactive restorations. الحشوات اللتجميلية الحديثة اصبحت محل اهتمام و غاية للاطفال في العالم الحديث .يتطلب الحشوات التجميلية أنظمة لاصقة قوية ؛أحد الاهتمامات الرئيسية في استخدام الأنظمة اللاصقة هو الحصول على رابطة كافية بين الحشوات وأنسجة الأسنان. يعد تحضير أنسجة الأسنان قبل عمل الحشوات خطوة مهمة في بروتوكول اللصق الذي يحدد نجاح العلاج. يعتبر الارتباط بالعاج أكثر صعوبة من الارتباط بالمينا بسبب النمط الأنبوبي للعاج ، وارتفاع محتوى الماء ، ووجود طبقة اللطاخة ، والتغيرات الفيزيولوجية المرضية مثل وجود عاج شديد التمعدن ومتصلب.تهدف هذه الدراسة إلى تقييم تأثير استخدام إشعاع ليزر الدايود على قوة الترابط بين مادتين ترميميتين تجميليتين ؛Activa والكومبوزت.
تم جمع مائة وأربعة أضراس لبنية وتقسيمها إلى مجموعتين رئيسيتين (ليزر وبدون ليزر). تم تركيب الأسنان في قوالب أكريليك وتجهيزها لكشف أسطح المينا وعاج الأسنان. تم توزيع عينات كل مجموعة عشوائيًا إلى 4 مجموعات فرعية: المجموعة الفرعية 1: حشو Activa المرتبط بالمينا ، المجموعة الفرعية 2: حشوActiva المرتبط بالعاج ، المجموعة الفرعية 3: حشو كومبوزت مرتبط بركيزة المينا والمجموعة الفرعية 4: حشو كومبوزت مرتبط بركيزة العاج .تم استخدام المادة اللاصقة العامة لعينات الكومبوزت و Activa في العاج ، بينما تم حفر عينات المينا بشكل انتقائي. تم تطبيق إشعاع ليزر الدايود (الطول الموجي 980 نانومتر ، الطاقة 1 واط ، الوضع المستمر) بعد تطبيق المادة اللاصقة وقبل البلمرة. بعد التدوير الحراري لمدة 500 دورة ، تم إجراء اختبار السندات المصغرة باستخدام آلة اختبار عامة. تم إجراء التحليل الإحصائي باستخدام ثلاث طرق ANOVA.
كان متوسط قوة الرابطة لعينات المينا أعلى بكثير من عينات العاج (P <0.05). لم يحسن التشعيع بليزر الدايود بشكل كبير متوسط قوة الرابطة الدقيقة في عينات المينا وعاج الأسنان. في عينات Activa ، قلل تشعيع ليزر الدايود بشكل كبير من قوة الرابطة الدقيقة في المينا والعاج. يمكن الاستنتاج أن تشعيع ليزر الدايود لم يحسن قوة الترابط لحشوات الكومبوزت عند تطبيقها قبل بلمرة المادة اللاصقة وكان لها تأثير سلبي على قوة الرابطة لترميمات Activa.
Text in English and abstract in Arabic & English.
Pediatric Dentistry
Bond strength Diode laser Primary molars Activa Bioactive Composite resin