Evaluation of the Efficacy of Sodium Dichloroisocyanurate and Calcium Hydroxide as Intra-Canal Medicaments on Microhardness of Radicular Dentin: A Comparative In-Vitro Study/
Sally Tarek El-Rashidy,
Evaluation of the Efficacy of Sodium Dichloroisocyanurate and Calcium Hydroxide as Intra-Canal Medicaments on Microhardness of Radicular Dentin: A Comparative In-Vitro Study/ /دراسة مقارنة بین تأثیر ثنائي كلورو إیزوسیانورات الصودیوم وھیدروكسید الكالسیوم كأدویة داخل قناة العصب على الصالدة والھیكل الكیمیائى للعاج Sally Tarek El-Rashidy ; Supervisors: Assoc. Prof. Dr. Heba Ahmed El- Asfouri, Assoc. Prof. Dr. Marwa Mahmoud Bedier, Dr. Dina Ahmed Aly Morsy. - 97 pages : illustrations ; 25 cm. + CD.
Thesis (M.Sc.) -Cairo University, 2023.
Bibliography: pages 81-94.
Aim: The aim of the present study was to evaluate the efficacy of Sodium dichloroisocyanurate
(NaDCC) compared to Calcium hydroxide (Ca(OH)2) as intracanal medicaments in terms of
superficial chemical structure and microhardness.
Methods: Sixty human dentin discs were obtained from single-rooted premolars, and randomly
allocated into 4 groups (n=15); NaDCC group, Ca(OH)2 group, N-S group (control), N-Na group
(control). After 1 and 4 weeks, Phosphate/amide I ratio (PO4/amide I) was evaluated by FTIR then
dentin microhardness was assessed.
Results: The results of PO4/amide I ratio showed a statistically significant difference between
NaDCC, Ca(OH)2 and NaOCl after 4 weeks (p<0.001). The results of microhardness showed no
statistically significant difference between all tested groups after 1 week (p=0.337) while, after 4
weeks, NaDCC showed a statistically significant difference when compared to Ca(OH)2 and NaOCl
groups (p<0.001).
Conclusions: The use of Ca(OH)2 for 4 weeks reduced dentin microhardness, whereas NaDCC did
not result in any change in the microhardness value. However, a change in PO4/amide I ratio was
observed earlier after 1 week in both Ca(OH)2 and NaOCl groups.
Keywords: Calcium hydroxide; dentin; hardness tests; sodium dichloroisocyanurate; EDTA; NaOCl;
intracanal medicament; superficial chemical structure; FTIR.
يعد التنضير الميكانيكي والكيميائي الكامل لقناة الجذر أمرا بالغ األهمية لنجاح المعالجة اللبية ألن البكتيريا المتبقية قد تؤثر سلبا
على نتيجة العالج. وقد تم اعتبار استخدام األدوية داخل القناة كوسيط مساهم في إجراءات المعالجة اللبية. أهم خصائص األدوية داخل
الجمجمة هي توافقها الحيوي واستقرارها والتأثيرات المضادة للبكتيريا دون تلف للمضيف. لذا، فإن الهدف من هذه الدراسة هو تقييم
آثار هيدروكسيدالكالسيوم وثنائي كلوروأيزوسيانورات الصوديومكأدويةداخل القناة على الصالبةالدقيقة والتركيب الكيميائي السطحي
للعاج الجذري.
تم تحضير معجون ثنائي كلوروأيزوسيانورات الصوديوم عن طريق طحن قرصين ) 5 جممن مسحوق NaDCC). ثم تم خلط
المسحوق مع محلول مخزن بالفوسفات لتشكيل مزيج كريمي. تم تعبئة العجينة في حقنة 3 سم. تم استخدام دواء تجاري لهيدروكسيد
الكالسيوم داخل القناة. تم تقسيم خمسة عشر ضواحك سفليةأحاديةالجذور رأسيا وأفقيا لتشكيل 4 عينات من كل سن. تم تقسيم ستين عينة
إلى أربع مجموعات متساوية)ن = 55(. المجموعة )أ( ثنائي كلوروأيزوسيانورات الصوديوم، المجموعة)ب( هيدروكسيد الكالسيوم،
المجموعة )ج( محلول ملحي، المجموعة )د( هيبوكلوريت الصوديوم. كان قياس العينات في أسبوع و4 أسابيع. تم وضع كل عينة في
كوب عينة مخروطي سعة 2 مل يحتوي علي 2 مل من المعاجين والمحلول الملحي لمجموعة التحكم و ٪2.5 هيبوكلوريت الصوديوم
للمجموعة الخالية من األدوية. بعد كل مدة زمنية تم فحص كل عينة باستخدام االنعكاس الكلي الموهن- قياس الطيف باألشعة تحت
الحمراء لتحويل فورييه الذي يحلل الفقد النسبي للمكونات العضوية وغير العضوية باستخدام نسب الفوسفات / األميد 5 ثم تم إجراء
اختبار فيكر للصالبة الدقيقة.
أظهرت نتائج دراستنا أنه لوحظ انخفاض جذري في متوسط الصالبة الدقيقة في مجموعة هيدروكسيد الكالسيوم بعد 4
أسابيع)0.001>P). ، في حين أن االختالفات لم تكن ذات داللة إحصائية في ثنائى كلورو أيزوسيانورات الصوديوم ومجموعة التحكم
حيث )0.601 0.192,=P )علي التوالي. كانت كمية الخفض التي يسببها ثنائي كلوروأيزوسيانورات الصوديوم قابلة للمقارنة مع
هيبوكلوريت الصوديوم. لوحظ أيضا زيادة معنوية في متوسط نسبة الفوسفات / األميد | في مجموعة هيدروكسيد الكالسيوم مقارنة مع
ثنائي كلوروأيزوسيانورات الصوديوم ومجموعة التحكم السليمة بعد أسبوع واحد، والتي لم تتغير بشكل ملحوظ خالل فترة المالحظة.
استنتجت هذه الدراسة أن استخدام هيدروكسيد الكالسيوم لمدة 4 أسابيع قلل من صالبة العاج الدقيقة، في حين أن ثنائي
كلوروأيزوسيانورات الصوديوم لم ينتج عنه أي تغيير في قيمة الصالبة الدقيقة. ومع ذلك، لوحظ تغيير في التركيب الكيميائي السطحي
في وقت سابق بعد 5 أسبوع في كل من مجموعات هيدروكسيد الكالسيوم وهيبوكلوريت الصوديوم.
Text in English and abstract in Arabic & English.
Dentistry
Calciumhydroxide;dentin dentin hardnesstests sodiumdichloroisocyanurate EDTA NaOCl intracanalmedicament superficialchemicalstructure FTIR
617.6
Evaluation of the Efficacy of Sodium Dichloroisocyanurate and Calcium Hydroxide as Intra-Canal Medicaments on Microhardness of Radicular Dentin: A Comparative In-Vitro Study/ /دراسة مقارنة بین تأثیر ثنائي كلورو إیزوسیانورات الصودیوم وھیدروكسید الكالسیوم كأدویة داخل قناة العصب على الصالدة والھیكل الكیمیائى للعاج Sally Tarek El-Rashidy ; Supervisors: Assoc. Prof. Dr. Heba Ahmed El- Asfouri, Assoc. Prof. Dr. Marwa Mahmoud Bedier, Dr. Dina Ahmed Aly Morsy. - 97 pages : illustrations ; 25 cm. + CD.
Thesis (M.Sc.) -Cairo University, 2023.
Bibliography: pages 81-94.
Aim: The aim of the present study was to evaluate the efficacy of Sodium dichloroisocyanurate
(NaDCC) compared to Calcium hydroxide (Ca(OH)2) as intracanal medicaments in terms of
superficial chemical structure and microhardness.
Methods: Sixty human dentin discs were obtained from single-rooted premolars, and randomly
allocated into 4 groups (n=15); NaDCC group, Ca(OH)2 group, N-S group (control), N-Na group
(control). After 1 and 4 weeks, Phosphate/amide I ratio (PO4/amide I) was evaluated by FTIR then
dentin microhardness was assessed.
Results: The results of PO4/amide I ratio showed a statistically significant difference between
NaDCC, Ca(OH)2 and NaOCl after 4 weeks (p<0.001). The results of microhardness showed no
statistically significant difference between all tested groups after 1 week (p=0.337) while, after 4
weeks, NaDCC showed a statistically significant difference when compared to Ca(OH)2 and NaOCl
groups (p<0.001).
Conclusions: The use of Ca(OH)2 for 4 weeks reduced dentin microhardness, whereas NaDCC did
not result in any change in the microhardness value. However, a change in PO4/amide I ratio was
observed earlier after 1 week in both Ca(OH)2 and NaOCl groups.
Keywords: Calcium hydroxide; dentin; hardness tests; sodium dichloroisocyanurate; EDTA; NaOCl;
intracanal medicament; superficial chemical structure; FTIR.
يعد التنضير الميكانيكي والكيميائي الكامل لقناة الجذر أمرا بالغ األهمية لنجاح المعالجة اللبية ألن البكتيريا المتبقية قد تؤثر سلبا
على نتيجة العالج. وقد تم اعتبار استخدام األدوية داخل القناة كوسيط مساهم في إجراءات المعالجة اللبية. أهم خصائص األدوية داخل
الجمجمة هي توافقها الحيوي واستقرارها والتأثيرات المضادة للبكتيريا دون تلف للمضيف. لذا، فإن الهدف من هذه الدراسة هو تقييم
آثار هيدروكسيدالكالسيوم وثنائي كلوروأيزوسيانورات الصوديومكأدويةداخل القناة على الصالبةالدقيقة والتركيب الكيميائي السطحي
للعاج الجذري.
تم تحضير معجون ثنائي كلوروأيزوسيانورات الصوديوم عن طريق طحن قرصين ) 5 جممن مسحوق NaDCC). ثم تم خلط
المسحوق مع محلول مخزن بالفوسفات لتشكيل مزيج كريمي. تم تعبئة العجينة في حقنة 3 سم. تم استخدام دواء تجاري لهيدروكسيد
الكالسيوم داخل القناة. تم تقسيم خمسة عشر ضواحك سفليةأحاديةالجذور رأسيا وأفقيا لتشكيل 4 عينات من كل سن. تم تقسيم ستين عينة
إلى أربع مجموعات متساوية)ن = 55(. المجموعة )أ( ثنائي كلوروأيزوسيانورات الصوديوم، المجموعة)ب( هيدروكسيد الكالسيوم،
المجموعة )ج( محلول ملحي، المجموعة )د( هيبوكلوريت الصوديوم. كان قياس العينات في أسبوع و4 أسابيع. تم وضع كل عينة في
كوب عينة مخروطي سعة 2 مل يحتوي علي 2 مل من المعاجين والمحلول الملحي لمجموعة التحكم و ٪2.5 هيبوكلوريت الصوديوم
للمجموعة الخالية من األدوية. بعد كل مدة زمنية تم فحص كل عينة باستخدام االنعكاس الكلي الموهن- قياس الطيف باألشعة تحت
الحمراء لتحويل فورييه الذي يحلل الفقد النسبي للمكونات العضوية وغير العضوية باستخدام نسب الفوسفات / األميد 5 ثم تم إجراء
اختبار فيكر للصالبة الدقيقة.
أظهرت نتائج دراستنا أنه لوحظ انخفاض جذري في متوسط الصالبة الدقيقة في مجموعة هيدروكسيد الكالسيوم بعد 4
أسابيع)0.001>P). ، في حين أن االختالفات لم تكن ذات داللة إحصائية في ثنائى كلورو أيزوسيانورات الصوديوم ومجموعة التحكم
حيث )0.601 0.192,=P )علي التوالي. كانت كمية الخفض التي يسببها ثنائي كلوروأيزوسيانورات الصوديوم قابلة للمقارنة مع
هيبوكلوريت الصوديوم. لوحظ أيضا زيادة معنوية في متوسط نسبة الفوسفات / األميد | في مجموعة هيدروكسيد الكالسيوم مقارنة مع
ثنائي كلوروأيزوسيانورات الصوديوم ومجموعة التحكم السليمة بعد أسبوع واحد، والتي لم تتغير بشكل ملحوظ خالل فترة المالحظة.
استنتجت هذه الدراسة أن استخدام هيدروكسيد الكالسيوم لمدة 4 أسابيع قلل من صالبة العاج الدقيقة، في حين أن ثنائي
كلوروأيزوسيانورات الصوديوم لم ينتج عنه أي تغيير في قيمة الصالبة الدقيقة. ومع ذلك، لوحظ تغيير في التركيب الكيميائي السطحي
في وقت سابق بعد 5 أسبوع في كل من مجموعات هيدروكسيد الكالسيوم وهيبوكلوريت الصوديوم.
Text in English and abstract in Arabic & English.
Dentistry
Calciumhydroxide;dentin dentin hardnesstests sodiumdichloroisocyanurate EDTA NaOCl intracanalmedicament superficialchemicalstructure FTIR
617.6