Mohamed Hassan Abdelghani Abdelaziz
Effect of ceramic nano - particles on wear and corrosion properties of aluminium silicon hypereutectic cast alloys (A390) / A390 تأثير الإضافات النانوية على خواص البرى والتأكل الكيميائى لمسبوكات الألومنيوم سيليكون الفوق يوتيكتيكية Mohamed Hassan Abdelghani Abdelaziz ; Supervised Yehia M. S. Shash , Iman S. Elmahallawi , Ragaie M. Rashad - Cairo : Mohamed Hassan Abdelghani Abdelaziz , 2012 - 105P. : charts , facsimiles ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Mechanical Design and Production
Hypereutectic aluminium - silicon cast alloy (A390) was used as the matrix and the reinforcing particles were alumina and titanium dioxide both are in the nano - scale with size ranges from 40-50 nm . The nano - particles with different weight fractions and mixture were stirred in the matrix in both semi - solid and liquid states . The result support the idea that the introduction of nano- particles induces a refining role to the microstructural features
Hypereutectic AISi cast alloys Nano- dispersion Semisolid processing
Effect of ceramic nano - particles on wear and corrosion properties of aluminium silicon hypereutectic cast alloys (A390) / A390 تأثير الإضافات النانوية على خواص البرى والتأكل الكيميائى لمسبوكات الألومنيوم سيليكون الفوق يوتيكتيكية Mohamed Hassan Abdelghani Abdelaziz ; Supervised Yehia M. S. Shash , Iman S. Elmahallawi , Ragaie M. Rashad - Cairo : Mohamed Hassan Abdelghani Abdelaziz , 2012 - 105P. : charts , facsimiles ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Mechanical Design and Production
Hypereutectic aluminium - silicon cast alloy (A390) was used as the matrix and the reinforcing particles were alumina and titanium dioxide both are in the nano - scale with size ranges from 40-50 nm . The nano - particles with different weight fractions and mixture were stirred in the matrix in both semi - solid and liquid states . The result support the idea that the introduction of nano- particles induces a refining role to the microstructural features
Hypereutectic AISi cast alloys Nano- dispersion Semisolid processing