Influence of heat treatment on the fracture toughness and microstructure of yttria-zirconia ceramics : An in vitro study /
Hashem Mohammed Salem Alqudaimi
Influence of heat treatment on the fracture toughness and microstructure of yttria-zirconia ceramics : An in vitro study / تأثير المعالجة الحرارية على صلابة الكسر و الهيكل الجزئي لسيراميك الاتريا زركونيا Hashem Mohammed Salem Alqudaimi ; Supervised Omaima S. Elmahallawi , Omnia A. Elshehy - Cairo : Hashem Mohammed Salem Alqudaimi , 2011 - 82 Leaves : charts , facsimiles ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Prosthodontics
The principle aim of this investigation was to evaluate the influence of heat treatment on the fracture toughness and microstructure of yttria-stabilized tetragonal zirconia polycrystals (Y-TZP) substrate. Forty ceramic dises (10-mm x 4-mm) were prepared from YZ blocks using CAD/CAM technology, and divided into four groups according to frequency of the heat treatments, ten samples for each group
Fracture toughness Heat treatment Y-TZP ceramic
Influence of heat treatment on the fracture toughness and microstructure of yttria-zirconia ceramics : An in vitro study / تأثير المعالجة الحرارية على صلابة الكسر و الهيكل الجزئي لسيراميك الاتريا زركونيا Hashem Mohammed Salem Alqudaimi ; Supervised Omaima S. Elmahallawi , Omnia A. Elshehy - Cairo : Hashem Mohammed Salem Alqudaimi , 2011 - 82 Leaves : charts , facsimiles ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Prosthodontics
The principle aim of this investigation was to evaluate the influence of heat treatment on the fracture toughness and microstructure of yttria-stabilized tetragonal zirconia polycrystals (Y-TZP) substrate. Forty ceramic dises (10-mm x 4-mm) were prepared from YZ blocks using CAD/CAM technology, and divided into four groups according to frequency of the heat treatments, ten samples for each group
Fracture toughness Heat treatment Y-TZP ceramic