Chemical properties and biocompatibility of new synthesized calcium phosphate cement compared to two root canal repair materials /
Shaimaa Ismail Gawdat Mohamed
Chemical properties and biocompatibility of new synthesized calcium phosphate cement compared to two root canal repair materials / الخصائص الكيميائية والتجانس الحيوى لاسمنت جديد مصنع من الكالسيوم فوسفات مقارنة بمادتين لاصلاح قنوات الجذور Shaimaa Ismail Gawdat Mohamed ; Supervised Salsabyl Mohamed Ibrahim , Medhat Abdelrahman Kataia , Mohamed Aiad Abdelhamid - Cairo : Shaimaa Ismail Gawdat Mohamed , 2012 - 158Leaves : charts , facsimiles ; 30cm
Thesis (Ph.D.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Endodontics
Aim of the study : The aim of the present study was to synthesize and characterize a new calcium phosphate based root repair material (SCPC) and it's comparison with bioaggregate (BA) and mineral trioxide aggregate (MTA) . Conclusions : It was concluded that SCPC showed high levels of calcium ion release which decreased with progressive periods of hydration it was found that SCPC was biologically compatible
Bioaggregate Biocompatibility Calcium phosphate cement
Chemical properties and biocompatibility of new synthesized calcium phosphate cement compared to two root canal repair materials / الخصائص الكيميائية والتجانس الحيوى لاسمنت جديد مصنع من الكالسيوم فوسفات مقارنة بمادتين لاصلاح قنوات الجذور Shaimaa Ismail Gawdat Mohamed ; Supervised Salsabyl Mohamed Ibrahim , Medhat Abdelrahman Kataia , Mohamed Aiad Abdelhamid - Cairo : Shaimaa Ismail Gawdat Mohamed , 2012 - 158Leaves : charts , facsimiles ; 30cm
Thesis (Ph.D.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Endodontics
Aim of the study : The aim of the present study was to synthesize and characterize a new calcium phosphate based root repair material (SCPC) and it's comparison with bioaggregate (BA) and mineral trioxide aggregate (MTA) . Conclusions : It was concluded that SCPC showed high levels of calcium ion release which decreased with progressive periods of hydration it was found that SCPC was biologically compatible
Bioaggregate Biocompatibility Calcium phosphate cement