The effect of experimental 2% chlorhexidine Gel compared to calcium hydroxide paste as intracanal medicaments on fracture resistance and microhardness of root canal dentin : A comparative in-vitro study /
Mohamed Abdullah Mohamed
The effect of experimental 2% chlorhexidine Gel compared to calcium hydroxide paste as intracanal medicaments on fracture resistance and microhardness of root canal dentin : A comparative in-vitro study / تأثير هلام الكلوروهكسيدين 2% المختبر مقارنة بمعجون هيدروكسيد الكالسيوم كعلاجات داخل قنوات الجذور على الصلادة الدقيقة ومقاومة كسر عاج جذور الاسنان : دراسة معملية مقارنة Mohamed Abdullah Mohamed ; Supervised Medhat Abdalrahman Kataia , Dalia Yahia Zaki , Reham Seyam - Cairo : Mohamed Abdullah Mohamed , 2012 - 76 Leaves : charts , facsimiles ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Oral and dental Medicine - Department of Endodontics
Aim: This study was designed to prepare an experimental 2% chlorhexidine gel and evaluate its effect on radicular dentin's microhardness and fracture resistance compared to both calcium hydroxide paste and a mixture of chlorhexidine with calcium hydroxide. Conclusion: The mechanical properties of the root canal dentin decreases with the increase in the application time of the intracanal medicaments
Calcium hydroxide Chlorhexidine gel Poloxamer
The effect of experimental 2% chlorhexidine Gel compared to calcium hydroxide paste as intracanal medicaments on fracture resistance and microhardness of root canal dentin : A comparative in-vitro study / تأثير هلام الكلوروهكسيدين 2% المختبر مقارنة بمعجون هيدروكسيد الكالسيوم كعلاجات داخل قنوات الجذور على الصلادة الدقيقة ومقاومة كسر عاج جذور الاسنان : دراسة معملية مقارنة Mohamed Abdullah Mohamed ; Supervised Medhat Abdalrahman Kataia , Dalia Yahia Zaki , Reham Seyam - Cairo : Mohamed Abdullah Mohamed , 2012 - 76 Leaves : charts , facsimiles ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Oral and dental Medicine - Department of Endodontics
Aim: This study was designed to prepare an experimental 2% chlorhexidine gel and evaluate its effect on radicular dentin's microhardness and fracture resistance compared to both calcium hydroxide paste and a mixture of chlorhexidine with calcium hydroxide. Conclusion: The mechanical properties of the root canal dentin decreases with the increase in the application time of the intracanal medicaments
Calcium hydroxide Chlorhexidine gel Poloxamer