The feasibility of nano-alumina deposition on yttria partially stabilized zirconia (Y-TZP) in enhancing its bond strength to dental resin cement /
Sherine Sherif Kamal Stino
The feasibility of nano-alumina deposition on yttria partially stabilized zirconia (Y-TZP) in enhancing its bond strength to dental resin cement / خدوى ترسيب النانو ألومينا على الزركونيا المستقرة جزئيا باليتريا فى تعزيز رابطتها بالأسمنت الراتنجى Sherine Sherif Kamal Stino ; Supervised Azza Abdelzaher Hashem , Madiha Ahmed Shoeib , Dalia Mohamed Abdelhamid - Cairo : Sherine Sherif Kamal Stino , 2013 - 130 Leaves : charts , facsimiles ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Dental Materials
Objectives: The aim of the study was to develop a predictable controlled method for the precipitation of nano-alumina coating as a surface treatment in trial to improve zirconia /resin bonding and to determine the durability of bond between coated samples and commercially available resin cement. Conclusions. The deposition method of nano-alumina is a promising, yet complex method to be used on zirconia substrate according to both mechanisms. Meticulous selection of alumina precursors, pH, temperature and stirring time as crucial and sensitive parameters in co-precipitation of alumina on zirconia substrates. Aluminum nitride is a more suitable precursor for nano-alumina deposition from suspension on zirconia substrate.The use of sulfuric acid as an innovative surface pre-coating method to the zirconia indicates its direct beneficial influence on surface roughness and bond strength of zirconia substrates with adhesive cement resin.Control polished specimens had a negative influence on strength showing the lowest shear bond strength values to adhesive resin cement of all subgroups
Adhesion Surface treatment Zirconia
The feasibility of nano-alumina deposition on yttria partially stabilized zirconia (Y-TZP) in enhancing its bond strength to dental resin cement / خدوى ترسيب النانو ألومينا على الزركونيا المستقرة جزئيا باليتريا فى تعزيز رابطتها بالأسمنت الراتنجى Sherine Sherif Kamal Stino ; Supervised Azza Abdelzaher Hashem , Madiha Ahmed Shoeib , Dalia Mohamed Abdelhamid - Cairo : Sherine Sherif Kamal Stino , 2013 - 130 Leaves : charts , facsimiles ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Dental Materials
Objectives: The aim of the study was to develop a predictable controlled method for the precipitation of nano-alumina coating as a surface treatment in trial to improve zirconia /resin bonding and to determine the durability of bond between coated samples and commercially available resin cement. Conclusions. The deposition method of nano-alumina is a promising, yet complex method to be used on zirconia substrate according to both mechanisms. Meticulous selection of alumina precursors, pH, temperature and stirring time as crucial and sensitive parameters in co-precipitation of alumina on zirconia substrates. Aluminum nitride is a more suitable precursor for nano-alumina deposition from suspension on zirconia substrate.The use of sulfuric acid as an innovative surface pre-coating method to the zirconia indicates its direct beneficial influence on surface roughness and bond strength of zirconia substrates with adhesive cement resin.Control polished specimens had a negative influence on strength showing the lowest shear bond strength values to adhesive resin cement of all subgroups
Adhesion Surface treatment Zirconia