An In vitro comparative study of Shear bond strength and microleakage of two different restorative materials used in the restoration of primary teeth /
Reham Ali Maher Elsayed
An In vitro comparative study of Shear bond strength and microleakage of two different restorative materials used in the restoration of primary teeth / دراسة معملية مقارنة الألتصاق القصى والتسرب الدقيق لاثنين من مواد حشو الأسنان المستخدمة فى الاسنان اللبنية Reham Ali Maher Elsayed ; Supervised Adel Abdelazim Elbardissy , Fatma Ahmed Hamdy Elshehaby , Nadia Amin Badr - Cairo : Reham Ali Maher Elsayed , 2013 - 94 Leaves : charts . facsimiles ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Pedodontics
The aim of this in vitro study was the evaluation and comparison of shear bond strength and microleakage of two nano restorative materials; nano composite and nano resin-modified glass ionomer, commonly used in the restoration of primary teeth. Results: There was a significant difference between the two restorative materials regarding shear bond strength while there was no significant difference between them regarding microleakage. Conclusions: Shear bond strength values of nano composite were significantly higher than nano resin modified glass ionomer. There was a statistically significant difference between modes of failure in the two groups. Nano composite showed lower microleakage values than nano resin modified glass ionomer; however, there was no statistically significant difference between them
Microleakage Nanocomposite Shear bond strength
An In vitro comparative study of Shear bond strength and microleakage of two different restorative materials used in the restoration of primary teeth / دراسة معملية مقارنة الألتصاق القصى والتسرب الدقيق لاثنين من مواد حشو الأسنان المستخدمة فى الاسنان اللبنية Reham Ali Maher Elsayed ; Supervised Adel Abdelazim Elbardissy , Fatma Ahmed Hamdy Elshehaby , Nadia Amin Badr - Cairo : Reham Ali Maher Elsayed , 2013 - 94 Leaves : charts . facsimiles ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Pedodontics
The aim of this in vitro study was the evaluation and comparison of shear bond strength and microleakage of two nano restorative materials; nano composite and nano resin-modified glass ionomer, commonly used in the restoration of primary teeth. Results: There was a significant difference between the two restorative materials regarding shear bond strength while there was no significant difference between them regarding microleakage. Conclusions: Shear bond strength values of nano composite were significantly higher than nano resin modified glass ionomer. There was a statistically significant difference between modes of failure in the two groups. Nano composite showed lower microleakage values than nano resin modified glass ionomer; however, there was no statistically significant difference between them
Microleakage Nanocomposite Shear bond strength