The effect of different irrigation regimens on the bond strength of three root canal sealers : An in vitro study /
Iman Abdosalam El kumati
The effect of different irrigation regimens on the bond strength of three root canal sealers : An in vitro study / تأثير أنظمة مختلفة للإرواء على قوة الرابط لثلاث أنواع مختلفة من لواصق القناة الجذرية Iman Abdosalam Elkumati ; Supervised Alaa Hussin Diab , Suzan Abdelwanees Amin , - Cairo : Iman Abdosalam El kumati , 2013 - 95 P. : charts , facsimiles ; 25cm
Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Endodontics
Aim of study: The aim of study is to compare the bond strength of a biocermic-based sealer, a mineral trioxide aggregate-based sealer and an epoxy resin based sealer to dentine when treated with different irrigation protocols. Material and methods: 90 freshly extracted straight single rooted human teeth, The roots were randomly divided into three main experimental groups according to the final irrigation regimen as follows: Group I (n=30): after complete instrumentation of prepared canals they were irrigated by 10ml of 2.6%(NaOCL) sodium hypochlorite and 5ml of distalled water. Group II (n=30): prepared canals were irrigated by 5ml of 2.6% NaOCL followed by 5ml of 17%(EDTA) then followed by 5ml distilled water for 1 min. Group III (n=30): prepared canals were irrigated by 5ml of 2.6% of NaOCL followed by 5ml of water then 5ml of 2% (CHX) Chlorohxidin. Each group was subdivided into three subgroups according to the sealer material to be used, as followed: - Sub group A (n=10): Biocermic-based sealer (i Root SP). Subgroup B (n=10): Epoxy resin based sealer cement (AH Plus). Sub group C (n=10): Mineral trioxide aggregate-based sealer (MTA Fillapex).One horizontal section of 2mm thickness, each was cut from middle thirds of each root were sliced to perform push out bond strenght measurement
AH Plus sealers i Root SP MTA Fillapex
The effect of different irrigation regimens on the bond strength of three root canal sealers : An in vitro study / تأثير أنظمة مختلفة للإرواء على قوة الرابط لثلاث أنواع مختلفة من لواصق القناة الجذرية Iman Abdosalam Elkumati ; Supervised Alaa Hussin Diab , Suzan Abdelwanees Amin , - Cairo : Iman Abdosalam El kumati , 2013 - 95 P. : charts , facsimiles ; 25cm
Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Endodontics
Aim of study: The aim of study is to compare the bond strength of a biocermic-based sealer, a mineral trioxide aggregate-based sealer and an epoxy resin based sealer to dentine when treated with different irrigation protocols. Material and methods: 90 freshly extracted straight single rooted human teeth, The roots were randomly divided into three main experimental groups according to the final irrigation regimen as follows: Group I (n=30): after complete instrumentation of prepared canals they were irrigated by 10ml of 2.6%(NaOCL) sodium hypochlorite and 5ml of distalled water. Group II (n=30): prepared canals were irrigated by 5ml of 2.6% NaOCL followed by 5ml of 17%(EDTA) then followed by 5ml distilled water for 1 min. Group III (n=30): prepared canals were irrigated by 5ml of 2.6% of NaOCL followed by 5ml of water then 5ml of 2% (CHX) Chlorohxidin. Each group was subdivided into three subgroups according to the sealer material to be used, as followed: - Sub group A (n=10): Biocermic-based sealer (i Root SP). Subgroup B (n=10): Epoxy resin based sealer cement (AH Plus). Sub group C (n=10): Mineral trioxide aggregate-based sealer (MTA Fillapex).One horizontal section of 2mm thickness, each was cut from middle thirds of each root were sliced to perform push out bond strenght measurement
AH Plus sealers i Root SP MTA Fillapex