Evaluation of the bond strength and the resin tag infiltration of flowable composite to primary dentin using different adhesive systems /
Wael Ziad Hesham
Evaluation of the bond strength and the resin tag infiltration of flowable composite to primary dentin using different adhesive systems / على عاج الأسنان اللبنية باستخدام أنظمة لاصقة مختلفة(Flowable) تقييم قوة الرابط وتغلغل النهايات الطرفية للراتنج المركب Wael Ziad Hesham ; Supervised Manal Ahmed Elsayed , Sherif Bahgat Eltawel - Cairo : Wael Ziad Hesham , 2014 - 76 P. : charts , facsimiles ; 25cm
Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Pedodontics
Objective: This study was performed to evaluate bond strength of a new self-etch self-adhesive / flowable composite in comparison with one step-self etch adhesive / flowable composite and two step total-etch adhesive / flowable composite. Materials and methods: Shear bond strength of the investigated material to middle dentin of primary teeth was evaluated after 24 hours. A total of thirty caries free , freshly extracted primary molar were utilized in this study. Teeth were divided into three groups according the material used (n = 10 per group). Buccal surface of acrylic embedded molars were ground into flat dentin surface ,to which material were applied according to manufacture instruction composite was applied split Teflon plate to form cylinders (2mmin diameter and 2mm in height)were constructed on the buccal surface of specimens to which shear-force was applied to a failure using A universal testing machine at a crosshead speed, 0.5mm/minute. After the test procedure, fractured surfaces were observed using a stereomicroscope (50X) to determine the failure mode. Representative sample per each group were investigated resin /dentin interface under scanning electron microscope
Adhesive systems Bond strength Resin tag Infiltration
Evaluation of the bond strength and the resin tag infiltration of flowable composite to primary dentin using different adhesive systems / على عاج الأسنان اللبنية باستخدام أنظمة لاصقة مختلفة(Flowable) تقييم قوة الرابط وتغلغل النهايات الطرفية للراتنج المركب Wael Ziad Hesham ; Supervised Manal Ahmed Elsayed , Sherif Bahgat Eltawel - Cairo : Wael Ziad Hesham , 2014 - 76 P. : charts , facsimiles ; 25cm
Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Pedodontics
Objective: This study was performed to evaluate bond strength of a new self-etch self-adhesive / flowable composite in comparison with one step-self etch adhesive / flowable composite and two step total-etch adhesive / flowable composite. Materials and methods: Shear bond strength of the investigated material to middle dentin of primary teeth was evaluated after 24 hours. A total of thirty caries free , freshly extracted primary molar were utilized in this study. Teeth were divided into three groups according the material used (n = 10 per group). Buccal surface of acrylic embedded molars were ground into flat dentin surface ,to which material were applied according to manufacture instruction composite was applied split Teflon plate to form cylinders (2mmin diameter and 2mm in height)were constructed on the buccal surface of specimens to which shear-force was applied to a failure using A universal testing machine at a crosshead speed, 0.5mm/minute. After the test procedure, fractured surfaces were observed using a stereomicroscope (50X) to determine the failure mode. Representative sample per each group were investigated resin /dentin interface under scanning electron microscope
Adhesive systems Bond strength Resin tag Infiltration