Temperature and field dependence of the magnetic and magnetoelectric properties of nanometric samarium strontium iron garnet doped bismuth /
Shereef Ahmed Ahmed Fareed
Temperature and field dependence of the magnetic and magnetoelectric properties of nanometric samarium strontium iron garnet doped bismuth / bismuthالنانومترى و المطعم بعنصر ال samarium strontium iron garnet تأثير كل من الحرارة و المجال المغناطيسى على الخواص المغناطيسية و المغنيطوكهربية للمتراكب Shereef Ahmed Ahmed Fareed ; Supervised Mohamed Ali Ahmed , Ebtesam Ateia Elfarahatey , Samiha Tadros Bishay - Cairo : Shereef Ahmed Ahmed Fareed , 2016 - 169 P. : photographs ; 25cm
Thesis (M.Sc.) - Cairo University - Faculty of Science - Department of Physics
Garnet nanoparticles of Sm Sr Fe O; (0.0x0.3) and 3-x x 5 12 Sm Bi Sr Fe O (0.0y0.15) were prepared by double sintering 2.8-y y 0.2 5 12 ceramic technique. X- ray diffraction analyses were carried out to study the role of strontium and bismuth content on the phase formation as well as on the lattice parameter, density, porosity and crystallite size of these samples. Scanning electron microscope and Energy dispersive X-ray for all prepared samples were carried out. The magnetic parameters were measured using faradays method in the range of temperature (300K-600K) at 1010, 1340 and 1660Oe. The vibrating sample magnetometer was used to measure the other essential magnetic parameters at (-20000H20000). The magnetoelectric coefficient of the samples were measured in presence of applied field from 650 to 2300Oe
Bismuth substitution magnetic susceptibility Garnet Strontium substitution
Temperature and field dependence of the magnetic and magnetoelectric properties of nanometric samarium strontium iron garnet doped bismuth / bismuthالنانومترى و المطعم بعنصر ال samarium strontium iron garnet تأثير كل من الحرارة و المجال المغناطيسى على الخواص المغناطيسية و المغنيطوكهربية للمتراكب Shereef Ahmed Ahmed Fareed ; Supervised Mohamed Ali Ahmed , Ebtesam Ateia Elfarahatey , Samiha Tadros Bishay - Cairo : Shereef Ahmed Ahmed Fareed , 2016 - 169 P. : photographs ; 25cm
Thesis (M.Sc.) - Cairo University - Faculty of Science - Department of Physics
Garnet nanoparticles of Sm Sr Fe O; (0.0x0.3) and 3-x x 5 12 Sm Bi Sr Fe O (0.0y0.15) were prepared by double sintering 2.8-y y 0.2 5 12 ceramic technique. X- ray diffraction analyses were carried out to study the role of strontium and bismuth content on the phase formation as well as on the lattice parameter, density, porosity and crystallite size of these samples. Scanning electron microscope and Energy dispersive X-ray for all prepared samples were carried out. The magnetic parameters were measured using faradays method in the range of temperature (300K-600K) at 1010, 1340 and 1660Oe. The vibrating sample magnetometer was used to measure the other essential magnetic parameters at (-20000H20000). The magnetoelectric coefficient of the samples were measured in presence of applied field from 650 to 2300Oe
Bismuth substitution magnetic susceptibility Garnet Strontium substitution