Effect of surface pretreatment on the remineralizing efficiency of different remineralizing agents /
Hanan Mohamed Abdel Aziz Elsherbiny
Effect of surface pretreatment on the remineralizing efficiency of different remineralizing agents / تأثير المعالجة القبلية للسطح على كفاءة اعادة التمعدن لعناصر التمعدن المختلفة Hanan Mohamed Abdel Aziz Elsherbiny ; Supervised Heba Salah Eldein Hamza , Dina Wafik Elkassas - Cairo : Hanan Mohamed Abdel Aziz Elsherbiny , 2016 - 103 P. : charts , facsimiles ; 25cm
Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Operative Dentistry
This research was designed to evaluate the effect of pretreatment by either acid etching or micro abrasion on the remineralizing potential of three different calcium phosphate based remineralizing agents using surface microhardnesss test. Materials & Methods: A total of 150 sound human mandibular molars were used in this study. Artificial enamel carious lesions were induced by immersing the specimens in a demineralizing solution for 4 days. The enamel specimens were divided randomly into three groups, according to the surface pretreatment modality, n=50. Group A1: no pretreatment (Control), Group A2: Acid etching using 35% Phosphoric acid and Group A3: micro-abrasion using microabrasion paste. Then they were all subdivided into five sub groups, n=10, according to the remineralizing agent used; Sub-group B1: molars stored in artificial saliva, Sub-group B2: fluoride varnish, Sub-group B3: CPP-ACP varnish, Sub-group B4: f-TCP varnish and finally Sub-group B5: Novamin paste. All products were applied according to the manufacturers instructions, and specimens were finally subjected to a pH cycling protocol of alternating demineralization (2 hours) and remineralization (22 hours) for eight consecutive days. The surface microhardness (SMH) was assessed using Vickers microhardness tester, prior to demineralization of the specimens as a baseline (SMH/Baseline), following demineralization (SMH/Demineralization) and finally, after the remineralization regimens & pH cycling (SMH/Remineralization), then mean surface microhardness recovery percentage was calculated SMHR %
Enamel demineralization Pretreatment Remineralization
Effect of surface pretreatment on the remineralizing efficiency of different remineralizing agents / تأثير المعالجة القبلية للسطح على كفاءة اعادة التمعدن لعناصر التمعدن المختلفة Hanan Mohamed Abdel Aziz Elsherbiny ; Supervised Heba Salah Eldein Hamza , Dina Wafik Elkassas - Cairo : Hanan Mohamed Abdel Aziz Elsherbiny , 2016 - 103 P. : charts , facsimiles ; 25cm
Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Operative Dentistry
This research was designed to evaluate the effect of pretreatment by either acid etching or micro abrasion on the remineralizing potential of three different calcium phosphate based remineralizing agents using surface microhardnesss test. Materials & Methods: A total of 150 sound human mandibular molars were used in this study. Artificial enamel carious lesions were induced by immersing the specimens in a demineralizing solution for 4 days. The enamel specimens were divided randomly into three groups, according to the surface pretreatment modality, n=50. Group A1: no pretreatment (Control), Group A2: Acid etching using 35% Phosphoric acid and Group A3: micro-abrasion using microabrasion paste. Then they were all subdivided into five sub groups, n=10, according to the remineralizing agent used; Sub-group B1: molars stored in artificial saliva, Sub-group B2: fluoride varnish, Sub-group B3: CPP-ACP varnish, Sub-group B4: f-TCP varnish and finally Sub-group B5: Novamin paste. All products were applied according to the manufacturers instructions, and specimens were finally subjected to a pH cycling protocol of alternating demineralization (2 hours) and remineralization (22 hours) for eight consecutive days. The surface microhardness (SMH) was assessed using Vickers microhardness tester, prior to demineralization of the specimens as a baseline (SMH/Baseline), following demineralization (SMH/Demineralization) and finally, after the remineralization regimens & pH cycling (SMH/Remineralization), then mean surface microhardness recovery percentage was calculated SMHR %
Enamel demineralization Pretreatment Remineralization