Reduction of iron ore fines for sponge iron production /
Abourehab Elmenshawy Hammam Hassan
Reduction of iron ore fines for sponge iron production / اختزال نواعم خام الحديد لإنتاج الحديد الإسفنجي Abourehab Elmenshawy Hammam Hassan ; Supervised Saad Megahed Elraghey , Abdelhady Abdelhady Elgeassy - Cairo : Abourehab Elmenshawy Hammam Hassan , 2018 - 105 P. : charts , facsimiles ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Metallurgical Engineering
The reduction of iron ore fines/charcoal or coal composite compacts was carried out isothermally at 900-1100oC and non-isothermally up to 1100C using different heating rates 5, 10, 15 and 20C/min in a flow of Ar gas. The reduction reaction of iron ore /C composite compacts was carried out using thermogravimetric (TG) and Quadruple Mass Spectrometer (QMS) techniques. TG technique was applied to measure the total mass loss resulted during the reduction process as a function of time. Alternatively, QMS was used for the quantitative analysis of CO and CO2 in the outlet gases from the reduction reactions at different time intervals. For iron ore fine compacts, the reduction reaction was performed isothermally at 800-1100oC and non-isothermally up to 1000C using different heating rates 5, 10, 15 and 20C/min with purified CO gas and the total mass loss resulted during the reduction process as a function of time was followed by TG technique. The different phases developed during reduction of compacts were identified by X-ray diffraction analysis and the average crystallite sizes were calculated from the obtained X-ray data. The structural changes accompanying the reduction process were examined with reflected light microscope (RLM) and with scanning electron microscope (SEM). The reduction kinetics and mechanism deduced from TG and QMS techniques were correlated and discussed
Direct reduction Non-coking coal Waste iron ore fines
Reduction of iron ore fines for sponge iron production / اختزال نواعم خام الحديد لإنتاج الحديد الإسفنجي Abourehab Elmenshawy Hammam Hassan ; Supervised Saad Megahed Elraghey , Abdelhady Abdelhady Elgeassy - Cairo : Abourehab Elmenshawy Hammam Hassan , 2018 - 105 P. : charts , facsimiles ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Metallurgical Engineering
The reduction of iron ore fines/charcoal or coal composite compacts was carried out isothermally at 900-1100oC and non-isothermally up to 1100C using different heating rates 5, 10, 15 and 20C/min in a flow of Ar gas. The reduction reaction of iron ore /C composite compacts was carried out using thermogravimetric (TG) and Quadruple Mass Spectrometer (QMS) techniques. TG technique was applied to measure the total mass loss resulted during the reduction process as a function of time. Alternatively, QMS was used for the quantitative analysis of CO and CO2 in the outlet gases from the reduction reactions at different time intervals. For iron ore fine compacts, the reduction reaction was performed isothermally at 800-1100oC and non-isothermally up to 1000C using different heating rates 5, 10, 15 and 20C/min with purified CO gas and the total mass loss resulted during the reduction process as a function of time was followed by TG technique. The different phases developed during reduction of compacts were identified by X-ray diffraction analysis and the average crystallite sizes were calculated from the obtained X-ray data. The structural changes accompanying the reduction process were examined with reflected light microscope (RLM) and with scanning electron microscope (SEM). The reduction kinetics and mechanism deduced from TG and QMS techniques were correlated and discussed
Direct reduction Non-coking coal Waste iron ore fines