Tribological and mechanical properties of aluminum matrix reinforced by CNTs / AL₂ O₃ /
Ahmed Shaban Abdelhamed Ali
Tribological and mechanical properties of aluminum matrix reinforced by CNTs / AL₂ O₃ / الخواص التريبولوجية والميكانيكية للألومنيوم المقوى بأنابيب الكربون النانوية وأكاسيد الالومنيوم Ahmed Shaban Abdelhamed Ali ; Supervised Tarek Abdelsadek Osman , Omayma Abdelgawad Elkady - Cairo : Ahmed Shaban Abdelhamed Ali , 2020 - 70 P. : charts , facsimiles ; 25cm
Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Mechanical Design and Production
The objective of this study is to Fabricate, Characterize, and Mechanical Properties Enhancement for Aluminum Matrix Reinforced by multi-walled carbon nanotubes (MWCNTs) and Aluminum Oxide (AL₂ O₃) and comparison of Aluminum Matrix before and after hot isostatic pressure (HIP)
Composite Materials Hot Isostatic Pressure (HIP) Tribology
Tribological and mechanical properties of aluminum matrix reinforced by CNTs / AL₂ O₃ / الخواص التريبولوجية والميكانيكية للألومنيوم المقوى بأنابيب الكربون النانوية وأكاسيد الالومنيوم Ahmed Shaban Abdelhamed Ali ; Supervised Tarek Abdelsadek Osman , Omayma Abdelgawad Elkady - Cairo : Ahmed Shaban Abdelhamed Ali , 2020 - 70 P. : charts , facsimiles ; 25cm
Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Mechanical Design and Production
The objective of this study is to Fabricate, Characterize, and Mechanical Properties Enhancement for Aluminum Matrix Reinforced by multi-walled carbon nanotubes (MWCNTs) and Aluminum Oxide (AL₂ O₃) and comparison of Aluminum Matrix before and after hot isostatic pressure (HIP)
Composite Materials Hot Isostatic Pressure (HIP) Tribology