Effect of nano-silver gel and calcium hydroxide paste on the bond strength of epoxy-resin based sealer to root canal dentin in anterior teeth : an in vitro study / [by] Hosam Abdelhady Ahmed Elbagalaty ; supervisors Professor Dr. Hany Samy Sadek, Dr. Dina Ahmed Morsy.

By:

Hosam Abdelhady Ahmed Elbagalaty [preparation.]

Contributor(s):

Material type: Text

TextLanguage: English Summary language: English, Arabic Producer: 2022Description: 110 pages : Illustrations ; 25 cm. + CDContent type:

text

Media type:

Unmediated

Carrier type:

volume

Other title:

تأثير جل النانوسيلفر ومعجون هيدروكسيد الكالسيوم على قوة الترابط لمادة السدادة القائمة على راتينج الايبوكسي إلى قناة الجذر في الأسنان الأمامية : دراسة في المختبر [Added title page title]

Subject(s):

DDC classification:

617.6 21

Available additional physical forms:

Issues also as CD.

Dissertation note: Thesis (M.Sc.)-Cairo University, 2022. Summary: The study aimed to evaluate and compare the Push-out bond strength of AH Plus root canal sealer after prior application of calcium hydroxide paste (Ca[OH]2) and Nano-silver gel intracanal placement on the bond strength of AH Plus (Dentsply DeTrey GmbH, Konstanz, Germany) in single-rooted human extracted maxillary incisors. Methodology: Root canals of 30 human extracted maxillary incisors were prepared with ProTaper System (Dentsply Maillefer, Ballaigues, Switzerland) up to master apical file # F5. Teeth were divided randomly into three groups according to the intracanal medication used. Group I: Control group (No intracanal medication), Group II: Nano-silver gel and Group III: Calcium hydroxide Ca(OH)2. After 3 weeks, the intracanal medications were removed by passive ultrasonic irrigation of 5 mL 2.5% NaOCl and final flush was done using 17% EDTA for 1 minute followed by 5 ml distilled water. Canals were filled using single-cone technique using master cone #F5 and AH plus sealer. After 1 week, a 2-mm-thick middle section of each root was then subjected to push-out testing using the universal testing machine. Results: There was a significant difference between the control group and the experimental groups (p<0.001). The highest value was found in control group (4.85±1.65), followed by calcium hydroxide (2.11±1.17), while the lowest value was found in nano-silver (1.41±1.08). Post hoc pairwise comparisons showed the control group to have a significantly higher value than other groups (p<0.001) with no statistically significant difference between calcium hydroxide and Nano-silver group. Conclusion: Prior calcium hydroxide and nano-silver placement seemed to decrease the push-out bond strength of epoxy resin-based Ah plus sealer.Summary: هدفت الدراسة إلى تقييم ومقارنة قوة رابطة الدفع للخارج لسداد قناة الجذر AH Plus بعد الاستخدام المسبق لمعجون هيدروكسيد الكالسيوم (Ca[OH]2) ووضع هلام النانو سيلفر داخل القناة على قوة الرابطة لـ AH Plus (Dentsply DeTrey). GmbH، كونستانز، ألمانيا) في القواطع العلوية المستخرجة من الإنسان ذات الجذر الواحد. المنهجية: تم تحضير قنوات الجذر لـ 30 قاطعة علوية مستخرجة من الإنسان باستخدام نظام ProTaper (Dentsply Maillefer، Ballaigues، سويسرا) حتى إتقان الملف القمي # F5. تم تقسيم الأسنان عشوائيا إلى ثلاث مجموعات وفقا للأدوية المستخدمة داخل القناة. المجموعة الأولى: المجموعة الضابطة (لا يوجد دواء داخل القناة)، المجموعة الثانية: هلام نانو الفضة والمجموعة الثالثة: هيدروكسيد الكالسيوم Ca(OH)2. بعد 3 أسابيع، تمت إزالة الأدوية داخل القناة عن طريق الري السلبي بالموجات فوق الصوتية لـ 5 مل 2.5% NaOCl وتم إجراء التدفق النهائي باستخدام 17% EDTA لمدة دقيقة واحدة متبوعًا بـ 5 مل ماء مقطر. تم ملئ القنوات بتقنية المخروط المفرد باستخدام المخروط الرئيسي #F5 و AH plus sealer. وبعد أسبوع واحد، تم بعد ذلك إخضاع القسم الأوسط بسمك 2 مم من كل جذر لاختبار الدفع باستخدام آلة الاختبار العامة. النتائج: كان هناك فرق كبير بين المجموعة الضابطة والمجموعات التجريبية (P <0.001). أعلى قيمة وجدت في المجموعة الضابطة (4.85±1.65)، يليها هيدروكسيد الكالسيوم (2.11±1.17)، بينما أقل قيمة وجدت في الفضة النانوية (1.41±1.08). أظهرت المقارنات الزوجية اللاحقة أن المجموعة الضابطة لديها قيمة أعلى بكثير من المجموعات الأخرى (P <0.001) مع عدم وجود فروق ذات دلالة إحصائية بين هيدروكسيد الكالسيوم ومجموعة نانو الفضة. الاستنتاج: يبدو أن وضع هيدروكسيد الكالسيوم والفضة النانوية مسبقًا يقلل من قوة رابطة الدفع للخارج في مادة Ah plus المانعة للتسرب القائمة على راتنجات الإيبوكسي

Tags from this library: No tags from this library for this title. Log in to add tags.

Average rating: 0.0 (0 votes)

Holdings
Item type	Current library	Home library	Call number	Status	Date due	Barcode
Thesis	قاعة الرسائل الجامعية - الدور الاول	المكتبة المركزبة الجديدة - جامعة القاهرة	Cai01.09.02.M.Sc.2022.Ho.E (Browse shelf(Opens below))	Not for loan		01010110087542000

Browsing المكتبة المركزبة الجديدة - جامعة القاهرة shelves Close shelf browser (Hides shelf browser)

Previous	No cover image available	No cover image available	No cover image available	No cover image available	No cover image available	No cover image available	No cover image available	Next
Previous	Cai01.09.02.M.Sc.2022.En.P Post-operative pain following glide path preparation using rotary neoniti gps file and manual k-files in non-vital lower molars: A Randomized controlled trial /	Cai01.09.02.M.Sc.2022.Ha.E Effect of glycolic acid as single irrigant versus sodium hypochlorite and edta on enterococcus faecalis count and smear layer removal in single rooted teeth : An In vitro study /	Cai01 09 02 M.Sc 2022 Hi.C A comparative scanning electron microscopic (sem) evaluation of the efficacy of brush file and xp endo finisher as irrigation activation methods in terms of smear layer removal and canal cleanliness in oval shaped canals /	Cai01.09.02.M.Sc.2022.Ho.E Effect of nano-silver gel and calcium hydroxide paste on the bond strength of epoxy-resin based sealer to root canal dentin in anterior teeth : an in vitro study /	Cai01.09.02.M.Sc.2022.Ma.C Comparison of the efficacy of prophylactic intraligamentary injection of piroxicam versus mepecaine for management of post-endodontic pain in posterior teeth : a randomized clinical trial : Therapeutic Study /	Cai01.09.02.M.Sc.2022.Ma.E Evaluation of the effect of casein phosphopeptide-amorphous calcium phosphate (cpp-acp) on edta treated root dentin microhardness when used as final irrigant in single rooted teeth : An in vitro study /	Cai01.09.02.M.Sc.2022.Ma.E Evaluation of the push-out bond strength and penetration of guttaflow bioseal, endoseal MTA and guttaflow 2 versus AH-Plus root canal sealers into the dentinal tubules in mandibular premolar teeth : a randomized in vitro comparative study /	Next

Thesis (M.Sc.)-Cairo University, 2022.

Bibliography: pages 90-107.

The study aimed to evaluate and compare the Push-out bond strength of AH Plus root canal sealer after prior application of calcium hydroxide paste (Ca[OH]2) and Nano-silver gel intracanal placement on the bond strength of AH Plus (Dentsply DeTrey GmbH, Konstanz, Germany) in single-rooted human extracted maxillary incisors.
Methodology: Root canals of 30 human extracted maxillary incisors were prepared with ProTaper System (Dentsply Maillefer, Ballaigues, Switzerland) up to master apical file # F5. Teeth were divided randomly into three groups according to the intracanal medication used. Group I: Control group (No intracanal medication), Group II: Nano-silver gel and Group III: Calcium hydroxide Ca(OH)2. After 3 weeks, the intracanal medications were removed by passive ultrasonic irrigation of 5 mL 2.5% NaOCl and final flush was done using 17% EDTA for 1 minute followed by 5 ml distilled water. Canals were filled using single-cone technique using master cone #F5 and AH plus sealer. After 1 week, a 2-mm-thick middle section of each root was then subjected to push-out testing using the universal testing machine.
Results: There was a significant difference between the control group and the experimental groups (p<0.001). The highest value was found in control group (4.85±1.65), followed by calcium hydroxide (2.11±1.17), while the lowest value was found in nano-silver (1.41±1.08). Post hoc pairwise comparisons showed the control group to have a significantly higher value than other groups (p<0.001) with no statistically significant difference between calcium hydroxide and Nano-silver group.
Conclusion: Prior calcium hydroxide and nano-silver placement seemed to decrease the push-out bond strength of epoxy resin-based Ah plus sealer.

هدفت الدراسة إلى تقييم ومقارنة قوة رابطة الدفع للخارج لسداد قناة الجذر AH Plus بعد الاستخدام المسبق لمعجون هيدروكسيد الكالسيوم (Ca[OH]2) ووضع هلام النانو سيلفر داخل القناة على قوة الرابطة لـ AH Plus (Dentsply DeTrey). GmbH، كونستانز، ألمانيا) في القواطع العلوية المستخرجة من الإنسان ذات الجذر الواحد.
المنهجية: تم تحضير قنوات الجذر لـ 30 قاطعة علوية مستخرجة من الإنسان باستخدام نظام ProTaper (Dentsply Maillefer، Ballaigues، سويسرا) حتى إتقان الملف القمي # F5. تم تقسيم الأسنان عشوائيا إلى ثلاث مجموعات وفقا للأدوية المستخدمة داخل القناة. المجموعة الأولى: المجموعة الضابطة (لا يوجد دواء داخل القناة)، المجموعة الثانية: هلام نانو الفضة والمجموعة الثالثة: هيدروكسيد الكالسيوم Ca(OH)2. بعد 3 أسابيع، تمت إزالة الأدوية داخل القناة عن طريق الري السلبي بالموجات فوق الصوتية لـ 5 مل 2.5% NaOCl وتم إجراء التدفق النهائي باستخدام 17% EDTA لمدة دقيقة واحدة متبوعًا بـ 5 مل ماء مقطر. تم ملئ القنوات بتقنية المخروط المفرد باستخدام المخروط الرئيسي #F5 و AH plus sealer. وبعد أسبوع واحد، تم بعد ذلك إخضاع القسم الأوسط بسمك 2 مم من كل جذر لاختبار الدفع باستخدام آلة الاختبار العامة.
النتائج: كان هناك فرق كبير بين المجموعة الضابطة والمجموعات التجريبية (P <0.001). أعلى قيمة وجدت في المجموعة الضابطة (4.85±1.65)، يليها هيدروكسيد الكالسيوم (2.11±1.17)، بينما أقل قيمة وجدت في الفضة النانوية (1.41±1.08). أظهرت المقارنات الزوجية اللاحقة أن المجموعة الضابطة لديها قيمة أعلى بكثير من المجموعات الأخرى (P <0.001) مع عدم وجود فروق ذات دلالة إحصائية بين هيدروكسيد الكالسيوم ومجموعة نانو الفضة.
الاستنتاج: يبدو أن وضع هيدروكسيد الكالسيوم والفضة النانوية مسبقًا يقلل من قوة رابطة الدفع للخارج في مادة Ah plus المانعة للتسرب القائمة على راتنجات الإيبوكسي

Issues also as CD.

Text in English and abstract in Arabic & English.

There are no comments on this title.

to post a comment.