Degradation of zirconia ceramics in water environment / Ezzat salah Eldin Elshazly ; Supervised Saad Megahed Elraghy , Hafez Abd El azzem Ahmed , Samia mohamed Elhout

By:

Ezzat salah Eldin Elshazly

Contributor(s):

Language: Eng Publication details: Cairo : Ezzat salah Eldin Elshazly , 2005Description: 79P : plans ; 30cmOther title:

تدهور خواص سيراميك الزركونيا فى الوسط المائى [Added title page title]

Subject(s):

Available additional physical forms:

Issued also as CD

Dissertation note: Thesis (M.Sc.) - Cairo University - Faculty Of Engineering - Department Of Metallurgical Engineering Summary: The ageing of the tetragonal zirconia polycrystals (Y - TZP) has been studied in hot water at 130c and pressure 2 bars for period of time up to 40 hours the test setup for performing the aging experiments was manufactured in the metallurgy department

Tags from this library: No tags from this library for this title. Log in to add tags.

Average rating: 0.0 (0 votes)

Holdings
Item type	Current library	Home library	Call number	Status	Barcode
Thesis	قاعة الرسائل الجامعية - الدور الاول	المكتبة المركزبة الجديدة - جامعة القاهرة	Cai01.13.12.M.Sc.2005.Ez.D. (Browse shelf(Opens below))	Not for loan	01010110044467000
CD - Rom	مخـــزن الرســائل الجـــامعية - البدروم	المكتبة المركزبة الجديدة - جامعة القاهرة	Cai01.13.12.M.Sc.2005.Ez.D. (Browse shelf(Opens below))	Not for loan	01020110044467000

Browsing المكتبة المركزبة الجديدة - جامعة القاهرة shelves Close shelf browser (Hides shelf browser)

Previous	No cover image available	No cover image available	No cover image available	No cover image available	No cover image available	No cover image available	No cover image available	Next
Previous	Cai01.13.12.M.Sc.2005.Al.E. Electrochemical behavior of powder metallurgy fabricated Ti3SiC2 /	Cai01.13.12.M.Sc.2005.El.E. Effect of rolling reduction on mechanical behaviour of aluminium alloy 6061 /	Cai01.13.12.M.Sc.2005.El.E. Effect of rolling reduction on mechanical behaviour of aluminium alloy 6061 /	Cai01.13.12.M.Sc.2005.Ez.D. Degradation of zirconia ceramics in water environment /	Cai01.13.12.M.Sc.2005.Ez.D. Degradation of zirconia ceramics in water environment /	Cai01.13.12.M.Sc.2005.Ko.N. Ni - yttria stabilized zirconia anode for solid oxide fuel cells /	Cai01.13.12.M.Sc.2005.Ko.N. Ni - yttria stabilized zirconia anode for solid oxide fuel cells /	Next

Thesis (M.Sc.) - Cairo University - Faculty Of Engineering - Department Of Metallurgical Engineering

The ageing of the tetragonal zirconia polycrystals (Y - TZP) has been studied in hot water at 130c and pressure 2 bars for period of time up to 40 hours the test setup for performing the aging experiments was manufactured in the metallurgy department