Shear bond strength of laser irradiated and silica coated in - ceram and zirconia based restorations / Bader Abdulsalam Mustafa Absah ; Supervised Lamiaa Sayed Kheiralla , Karl Hani Haleem

By: Contributor(s): Material type: TextTextLanguage: English Publication details: Cairo : Bader Abdulsalam Mustafa Absah , 2013Description: 104 Leaves : charts , facsimiles ; 30cmOther title:
  • قوة الربط القصية التغطية باشعة الليزر والتغطية بلسيليكا لترميمات الزركونيوم والأنسيرام [Added title page title]
Subject(s): Available additional physical forms:
  • Issued also as CD
Dissertation note: Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Prosthodontics Summary: The purpose of this study: was to evaluate the effect of carbon dioxide irradiation and silica coating surface treatment of in - ceram and zirconia cores on their surface roughness and shear bond strength to natural teeth . Results : Shear bond was significantly affected by surface treatment and type of ceramic which the highest bond strength values (MPa) were achieved by SC
Tags from this library: No tags from this library for this title. Log in to add tags.
Star ratings
    Average rating: 0.0 (0 votes)
Holdings
Item type Current library Home library Call number Copy number Status Barcode
Thesis Thesis قاعة الرسائل الجامعية - الدور الاول المكتبة المركزبة الجديدة - جامعة القاهرة Cai01.09.09.M.Sc.2013.Ba.S (Browse shelf(Opens below)) Not for loan 01010110062835000
CD - Rom CD - Rom مخـــزن الرســائل الجـــامعية - البدروم المكتبة المركزبة الجديدة - جامعة القاهرة Cai01.09.09.M.Sc.2013.Ba.S (Browse shelf(Opens below)) 62835.CD Not for loan 01020110062835000

Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Prosthodontics

The purpose of this study: was to evaluate the effect of carbon dioxide irradiation and silica coating surface treatment of in - ceram and zirconia cores on their surface roughness and shear bond strength to natural teeth . Results : Shear bond was significantly affected by surface treatment and type of ceramic which the highest bond strength values (MPa) were achieved by SC