Microtensile bond strength of direct resin composite to deep dentin using two adhesive systems with or without pretreatment of Tri Calcium Phosphate or Fluoride : In-vitro study / Amr Hani Hassan ; Supervised Inas Mohey Eldin , Hadeel Farouk

By:

Amr Hani Hassan

Contributor(s):

Material type: Text

TextLanguage: English Publication details: Cairo : Amr Hani Hassan , 2017Description: 73 P. : charts , facsimiles ; 25cmOther title:

قوة سندات الشد للراتنج المركب للعاج العميق باستخدام اثنين من نظم الاصقة مع أو بدون المعالجة الاوليه بواسطه ثلاثي فوسفات الكالسيوم أو الفلوريد : دراسة معملية [Added title page title]

Subject(s):

Available additional physical forms:

Issued also as CD

Dissertation note: Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Operative Dentistry Summary: The aim is to investigate the effect of two desensitizing agents as dentin surface pretreatments on microtensile bond strength of a direct resin composite restoration using two adhesive systems. In addition fracture mode of the specimens at dentin - restoration interface was studied. A total of 22 extracted molar teeth were selected. A flat dentin occlusal surface was prepared using a low speed diamond saw under water coolant. Teeth were randomly divided into three main groups according to surface pretreatment. First group, no dentin pretreatment (A1), second group Tricalciam phosphate (TCP) pretreatment and third group, Sodium fluoride (NaF) pretreatment (A3). Each group was further subdivided into two subgroups according to the adhesives used namely etch and rinse adhesive (B1) and self-etch adhesive (B2). A Teflon mold was used to build up resin composite; Teeth were sectioned in a longitudinal and a horizontal direction to obtain 0.9±0.1 mm in thickness beams. All samples were tested by universal testing machine to examine microtensile bond strength followed by measuring fracture mode at restoration-tooth interface by using a stereomicroscope. Under limitation of this study Tri calcium phosphate desensitizing agent can be used to treat hypersensitive dentin without deranged effect on MTBS at resin composite - dentin interface regardless of the adhesive used

Tags from this library: No tags from this library for this title. Log in to add tags.

Average rating: 0.0 (0 votes)

Holdings
Item type	Current library	Home library	Call number	Copy number	Status	Date due	Barcode
Thesis	قاعة الرسائل الجامعية - الدور الاول	المكتبة المركزبة الجديدة - جامعة القاهرة	Cai01.09.03.M.Sc.2017.Am.M (Browse shelf(Opens below))		Not for loan		01010110074002000
CD - Rom	مخـــزن الرســائل الجـــامعية - البدروم	المكتبة المركزبة الجديدة - جامعة القاهرة	Cai01.09.03.M.Sc.2017.Am.M (Browse shelf(Opens below))	74002.CD	Not for loan		01020110074002000

Browsing المكتبة المركزبة الجديدة - جامعة القاهرة shelves Close shelf browser (Hides shelf browser)

Previous	No cover image available	No cover image available	No cover image available	No cover image available	No cover image available	No cover image available	No cover image available	Next
Previous	Cai01.09.03.M.Sc.2017.Ah.I Influence of different modes of light emitting diodes (LED) on surface hardness and color stability of contemporary restoratives /	Cai01.09.03.M.Sc.2017.Al.W Wear resistance of ormocer (organically modified ceramics) and POSS (Polyhedral oligomericsilsesquioxane) versus methacrylate based nanohybrid resin composites: An in vitro study /	Cai01.09.03.M.Sc.2017.Al.W Wear resistance of ormocer (organically modified ceramics) and POSS (Polyhedral oligomericsilsesquioxane) versus methacrylate based nanohybrid resin composites: An in vitro study /	Cai01.09.03.M.Sc.2017.Am.M Microtensile bond strength of direct resin composite to deep dentin using two adhesive systems with or without pretreatment of Tri Calcium Phosphate or Fluoride : In-vitro study /	Cai01.09.03.M.Sc.2017.Am.M Microtensile bond strength of direct resin composite to deep dentin using two adhesive systems with or without pretreatment of Tri Calcium Phosphate or Fluoride : In-vitro study /	Cai01.09.03.M.Sc.2017.Am.S Surface roughness and color change of machinable ceramic, composite and hybrid blocks before and after erosion and/or abrasion challenge : In vitro study /	Cai01.09.03.M.Sc.2017.Am.S Surface roughness and color change of machinable ceramic, composite and hybrid blocks before and after erosion and/or abrasion challenge : In vitro study /	Next

Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Operative Dentistry

The aim is to investigate the effect of two desensitizing agents as dentin surface pretreatments on microtensile bond strength of a direct resin composite restoration using two adhesive systems. In addition fracture mode of the specimens at dentin - restoration interface was studied. A total of 22 extracted molar teeth were selected. A flat dentin occlusal surface was prepared using a low speed diamond saw under water coolant. Teeth were randomly divided into three main groups according to surface pretreatment. First group, no dentin pretreatment (A1), second group Tricalciam phosphate (TCP) pretreatment and third group, Sodium fluoride (NaF) pretreatment (A3). Each group was further subdivided into two subgroups according to the adhesives used namely etch and rinse adhesive (B1) and self-etch adhesive (B2). A Teflon mold was used to build up resin composite; Teeth were sectioned in a longitudinal and a horizontal direction to obtain 0.9±0.1 mm in thickness beams. All samples were tested by universal testing machine to examine microtensile bond strength followed by measuring fracture mode at restoration-tooth interface by using a stereomicroscope. Under limitation of this study Tri calcium phosphate desensitizing agent can be used to treat hypersensitive dentin without deranged effect on MTBS at resin composite - dentin interface regardless of the adhesive used