Factors influncing sintering of tungsten carbide - 10% cobalt /  
 العوامل التى تؤثر على تلبيد كربيد التنجستين 10 % كوبلت 
Janet Maher Zaki ; Supervised Magdi F. Abadir , Ibrahim Mohamed Ismail , Abdelhamid Mustafa Abdelhamid 
 - Cairo :   Janet Maher Zaki ,   2013 
 - 88 P. :   charts , facsimiles ;   30cm 
<br/><br/>Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Chemical Engineering 
<br/><br/> The objective of this thesis is to study the sintering characteristics of fine WC powder doped with 10% cobalt on the temperature range 1100 - 1300 C in inert atmosphere. WC- 10% Co tablets were prepared by using uniaxial dry pressing at different pressure (510 MPa, 765 MPa) the holding time used for firing tablets was raised to reach 3 hours . Densification parameters were determined at all sintering condation 
<br/><br/>
<br/><br/><label>Subjects--Index Terms: </label>Composite material  Sintering  Tungsten carbide