Influence of cement types and thicknesses on resin - zirconia shear bond strength /
تأثير أنواع و سماكات اللاصق على قوة الربط القصبية بين الراتنج و الزركونيا
Eshraq Fadhel Hamed Rajeh ; Supervised Shereen Adel Ameen , Mona Attaya Elagroudy
- Cairo : Eshraq Fadhel Hamed Rajeh , 2014
- 81 Leaves : facsimiles , photographs ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Prosthodontics
The aim of this study was to evaluate the influence of different cement thicknesses of two adhesive cements on resin - zirconia shear bond strength. Thirty zirconia discs were prepared from ICE zirconia block. Thirty freshly extracted molars were transversely sectioned at the deep dentin level and bonded to air-abraded zirconium oxide ceramic disks. The specimens were divided into two groups according to cement type: Rely X UniCem or Rely X ARC, and further subdivided into three subgroups according to cement thickness:50 om,100 om or 150 om. All cemented specimens were stored in distilled water for 2 weeks. Then thermocycled between 5oC and 55oC for 1000 cycles with a dwell time of 30 seconds and a transfer time of 2 seconds. All the samples were subjected to a shear test to evaluate their bond strengths. Two - way Analysis of Variance (ANOVA) was used in testing significance for the effect of cement type, cement thickness and their interactions on mean shear bond strength. All failures occurred at the resin - zirconia interface (adhesive failure). RelyX ARC with 100 æm thickness recorded the statistically significantly highest mean shear bond strength