TI  - Effect of thickness of nanofilled resin composite and nano-ionomer on the restoration{u2019}s colour and translucency / 
PY  - 2010///
CY  - Cairo : 
PB  - Nesrine Kamal Hammady , 
KW  - Nano-ionomer
KW  - Nanofilled resin composite
KW  - The restoration{u2019}s colour and translucency
N1  - Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Operative Dentistry; Issued also as CD
N2  - This study was conducted to evaluate the influence of different thickness of nanofilled resin composite and nanofilled glass ionomer restorative materials on its color and translucency. A total of sixty disc shaped specimens of 5 mm in diameter were prepared using a specially constructed hollow cylindrical copper mold with different movable bottoms which was used to produce specimens with the same diameter but with different thickness of 1, 1.5 and 2 mm thicknesses. 30 specimens were prepared from shade (A3) nanofilled resin composite; Filtek{u2122} Supreme XT, (3M, ESPE) and the other 30 were prepared from shade (A3) of  nano-Ionomer restorative material, ketac{u2122} N100 (3M, ESPE). From each restorative material 10 specimens were prepared from each thickness (1, 1.5, 2 mm).The specimens were cured using (Ivoclar vivadent) bluephase C5 light curing unit. The colorimetric values (L*, a* and b*) were measured using the spectrophotometer (UV-shimadzu 3101 pc-spectrophotometer) and the translucency was measured using the luminous diffuse transmittance (optical translucency) equation. Data was analyzed using two-way analysis of variance (ANOVA) and Tukey{u2019}s post hoc test