Kamilia Faisal Abdulkader

Shear bond strength of cemented zirconia-reinforced lithium silicate ceramics (celtra duo) with two surface treatments : In vitro study / دراسة معملية : تقييم قوه الربط القصيه للسيراميك الزجاجى المدعم بالزركونيا الملصقة و المعالج سطحها الخارجى بنوعين مختلفين من العلاج الخارجى Kamilia Faisal Abdulkader ; Supervised Gihan Abdelhady Elnaggar , Lamiaa Sayed Kheiralla - Cairo : Kamilia Faisal Abdulkader , 2019 - 81 P. : charts , facsmilies ; 25cm

Thesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine - Department of Prosthodontics

Enhance the bonding of cement to ceramic surface with a variety of ceramic surface modifications have been established. Air-abrasion using alumina particles, hydrofluoric acid has been shown to provide micromechanical interlocking at the ceramic-resin interface` The aim of the present study was to evaluate the effect of two surface treatments; acid etching and sandblasting; on the shear bond strength of cemented newly introduced zirconia-reinforced lithium silicate ceramics following thermocycling. Methods 24 discs of Zirconia- reinforced glass ceramics (celtra duo) were tested using 10% hydrofluoric acid for 20 seconds (control group) and 50 om aluminum oxide for 60 seconds at 10mm distance from the nozzle tip of sandblasting machine. Subsequent the surface treatments both groups were salinized and cemented to composites background discs using self-adhesive duel cure resin cement (BisCem). All sample were subjected to 2500 thermal cycle shear bond strength and failure mode was evaluated



Ceramics (celtra duo) Shear bond strength Zirconia-reinforced lithium silicate