TY  - BOOK
AU  - Sondos Ibrahim Soliman Eissa
AU  - Hanan Hasssan Aboalmaged , 
AU  - Shakinaz Alielden Elsherbiny , 
TI  - Comparative study on production methods of porous hydroxyapatite / 
PY  - 2021///
CY  - Cairo : 
PB  - Sondos Ibrahim Soliman Eissa , 
KW  - Hydroxyapatite
KW  - Porous ceramics
KW  - Starch consolidation casting
N1  - Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Chemical Engineering; Issued also as CD
N2  - Hydroxyapatite is one of the famous calcium phosphate bioceramics. In latest years, porous HA has attracted more attention due to its low density, high porosity, high specific area, and high bioactivity. Hydroxyapatite powder was synthesized and characterized using XRD, IR, TEM, SEM and both (TGA & DTG). Fabrication of hydroxyapatite into porous samples was carried out by three different casting methods (starch consolidation, direct coagulation and freeze gel casting methods) with three different HA powder contents and fired at three different firing temperatures. Porosity, density and mechanical compression strength were measured for all porous hydroxyapatite samples. All porous hydroxyapatite samples were characterized by XRD. SEM was used to study the microstructure of some selected porous HA samples. As a result of this work, pure hydroxyapatite powder was successively prepared by wet precipitation method. The results concluded that porous HA samples prepared by freeze gel casting method showed higher mechanical strength (50.2 MPa) and thermal stability until 1200 ⁰C than those prepared by other methods
UR  - http://172.23.153.220/th.pdf
ER  -