Influence of heat treatment conditions on the wear resistance and hot tensile properties of the Ti-6Al-4V alloy / Manar Nady Abdelghany Mansour ; Supervised Waleed Mohamed Khalifa , Shimaa Hasan Elhadad , Ahmed Yehia Shash

By:

Manar Nady Abdelghany Mansour

Contributor(s):

Material type: Text

TextLanguage: English Publication details: Cairo : Manar Nady Abdelghany Mansour , 2019Description: 52 P. : charts , facsimiles ; 30cmOther title:

تأثير ظروف المعالجة الحرارية على مقاومة البرى و خصائص الشد على الساخن لسبيكة تيتانيوم-6 ألومنيوم-4 فناديوم [Added title page title]

Subject(s):

Available additional physical forms:

Issued also as CD

Dissertation note: Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Metallurgical Engineering Summary: In the current work, several heat treatments were carried out below and above the beta transus temperature of the Ti-6Al-4V alloy. The resultant microstructures and their effects on hardness, wear resistance and hot tensile properties of the Ti-6Al-4V alloy were examined. The results showed that solution treatment of Ti-6Al-4V samples followed by water quenching from Ý and Ü/Ý fields raised the alloy hardness from 380 to 575 and 656 HV respectively while no remarkable changes were observed after aging. Hot tensile strength of the as-forged sample increased from 671 to 756 MPa after water quenching from the Ý-phase field, while the air cooling decreased the tensile strength 644 MPa. The fracture mode of the tensile samples was more ductile in case of the solution treated samples compared to the as forged samples. A subsurface layer was formed due to the diffusion of oxygen into the surface at high temperatures. This layer masked the differences of wear behavior of the specimens

Tags from this library: No tags from this library for this title. Log in to add tags.

Average rating: 0.0 (0 votes)

Holdings
Item type	Current library	Home library	Call number	Copy number	Status	Date due	Barcode
Thesis	قاعة الرسائل الجامعية - الدور الاول	المكتبة المركزبة الجديدة - جامعة القاهرة	Cai01.13.12.M.Sc.2019.Ma.I (Browse shelf(Opens below))		Not for loan		01010110078477000
CD - Rom	مخـــزن الرســائل الجـــامعية - البدروم	المكتبة المركزبة الجديدة - جامعة القاهرة	Cai01.13.12.M.Sc.2019.Ma.I (Browse shelf(Opens below))	78477.CD	Not for loan		01020110078477000

Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Metallurgical Engineering

In the current work, several heat treatments were carried out below and above the beta transus temperature of the Ti-6Al-4V alloy. The resultant microstructures and their effects on hardness, wear resistance and hot tensile properties of the Ti-6Al-4V alloy were examined. The results showed that solution treatment of Ti-6Al-4V samples followed by water quenching from Ý and Ü/Ý fields raised the alloy hardness from 380 to 575 and 656 HV respectively while no remarkable changes were observed after aging. Hot tensile strength of the as-forged sample increased from 671 to 756 MPa after water quenching from the Ý-phase field, while the air cooling decreased the tensile strength 644 MPa. The fracture mode of the tensile samples was more ductile in case of the solution treated samples compared to the as forged samples. A subsurface layer was formed due to the diffusion of oxygen into the surface at high temperatures. This layer masked the differences of wear behavior of the specimens

Issued also as CD