| 100 | 0 | _aMostafa Mahmoud Saleh Elshabrawy | |
| 245 | 1 | 0 |
_aEvaluating the shear bond Strength of 2SR Nexco Paste3 versus 2IPS Inline3 for veneering metal substructure : _bAn in vitro study / _cMostafa Mahmoud Saleh Elshabrawy ; Supervised Rana Mahmoud Sherif , Maha Taymour |
| 246 | 1 | 5 |
_aتقييم قوة الربط القصية لقشرة "اس ارنكسكو"مقارنة بقشرة 3اى بى اس ان لاين : لبنية معدنية : _bدراسه معملية |
| 260 |
_aCairo : _bMostafa Mahmoud Saleh Elshabrawy , _c2015 |
||
| 300 |
_a110 P. : _bfacsimiles ; _c25cm |
||
| 502 | _aThesis (M.Sc.) - Cairo University - Faculty of Oral and Dental Medicine- Department of Prosthodontics | ||
| 520 | _aPurpose: This In-Vitro study compared the shear bond strength between indirect composite and porcelain for veneering a metal substructure. Materials and Methods: twenty-four disks cast in nickel chromium alloy were divided equally into two groups and received different treatments for veneering: Indirect Composite (SR Nexco Paste) was applied on one group of specimens; the control group was veneered using porcelain (IPS Inline). The specimens were tested by a circular interface shear test after 2,500 thermocycles between 5{u00BA}C and 55{u00BA}C water baths with a dwell time of 20 seconds. The fractured specimens were evaluated to determine the mode of failure by a scanning electron microscope. Results: The mean shear bond strength values (in MPa) after thermocycling was 10.06 for the indirect composite group and 34.94 for the porcelain group. The metal-ceramic group exhibited significantly higher bond strength than the indirect composite group. Conclusion: SR Nexco can be considered as a reliable material for veneering a metal substructure according to ISO 1477 and Matsumura | ||
| 530 | _aIssued also as CD | ||
| 653 | 4 | _aIndirect Composite | |
| 653 | 4 | _aPorcelain | |
| 653 | 4 | _aShear bond strength | |
| 700 | 0 |
_aMahaTaymour , _eSupervisor |
|
| 700 | 0 |
_aRana Mahmoud Sherif , _eSupervisor |
|
| 905 |
_aAml _eCataloger |
||
| 905 |
_aNazla _eRevisor |
||
| 942 |
_2ddc _cTH |
||
| 999 |
_c56539 _d56539 |
||