Mechanical properties and durability of synthesized geopolymer composites based on metakaolin and other by-product materials / Eslam Ahmed Ahmed Mahmoud Elgabry ; Supervised Mohamed Ismail Abdelaziz Serag

By:

Eslam Ahmed Ahmed Mahmoud Elgabry

Contributor(s):

Mohamed Ismail Abdelaziz Serag []

Material type: Text

TextLanguage: English Publication details: Cairo : Eslam Ahmed Ahmed Mahmoud Elgabry , 2019Description: 72 P. : charts , facsimiles ; 30cmOther title:

الخواص الميكانيكية والتحمل مع الزمن لمركبات جيوبوليمريه من الميتاكاولين وبعض المخلفات الصناعيه الأخرى [Added title page title]

Subject(s):

Online resources:

Click here to access online

Available additional physical forms:

Issued also as CD

Dissertation note: Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Civil Engineering Summary: In this research, 19 different synthesized geopolymer composites were prepared and tested. These mixes were based on metakaolin as source material and different ratios of cement kiln dust, slag, silica fume, copper, and zinc dust.Compressive strength and durability were measured for all mixes cured by different techniques. Compressive strength were measured at 3, 7, 14, 28, and 90 days while durability was tested against and exposure to sea water, nitric acid and against fire at 400 oC temperature. The results show remarkable properties for some composites with respect to strength and durability

Tags from this library: No tags from this library for this title. Log in to add tags.

Average rating: 0.0 (0 votes)

Holdings
Item type	Current library	Home library	Call number	Copy number	Status	Barcode
Thesis	قاعة الرسائل الجامعية - الدور الاول	المكتبة المركزبة الجديدة - جامعة القاهرة	Cai01.13.05.M.Sc.2019.Es.M (Browse shelf(Opens below))		Not for loan	01010110080704000
CD - Rom	مخـــزن الرســائل الجـــامعية - البدروم	المكتبة المركزبة الجديدة - جامعة القاهرة	Cai01.13.05.M.Sc.2019.Es.M (Browse shelf(Opens below))	80704.CD	Not for loan	01020110080704000

Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Civil Engineering

In this research, 19 different synthesized geopolymer composites were prepared and tested. These mixes were based on metakaolin as source material and different ratios of cement kiln dust, slag, silica fume, copper, and zinc dust.Compressive strength and durability were measured for all mixes cured by different techniques. Compressive strength were measured at 3, 7, 14, 28, and 90 days while durability was tested against and exposure to sea water, nitric acid and against fire at 400 oC temperature. The results show remarkable properties for some composites with respect to strength and durability

Issued also as CD