Gas metal arc welding of 9%ni steel using non-conventional ferritic welding filler wire for LNG facilities /
Ahmed Mohamed Abou Al Soud Abd Al Rahman,
Gas metal arc welding of 9%ni steel using non-conventional ferritic welding filler wire for LNG facilities / اللحام القوسي بالمعدن والغاز لصلب 9% نيكل بإستخدام سلك حشو اللحام الفريتي غير التقليدي لحاويات الغاز الطبيعي المسال / by Ahmed Mohamed Abou Al Soud Abd Al Rahman ; Supervisors Prof. M.R.El-Koussy, Prof. Nahed A.Abd El-Raheem, Prof. Waleed A.Khalifa, Prof.A.El-Batahgy. - 102 pages : illustrations ; 30 cm. + CD.
Thesis (Ph.D)-Cairo University, 2024.
Bibliography: pages 97-102.
The facilities which used to store LNG are constructed from nine percent Nickel Steel using GMAW, the conventional/common choice is Nickel-Based consumable (ERNiCrMo-3).Under matching base metal due to strength loss significantly increase the manufacturing cost as a result of increasing the joint thickness in order to retain the strength as well as a significant amount is required for filling the Weldments. When using the non-conventional matching ferritic filler wire (ERNi11), Compared to basic material, the resulting tensile strength is greater, as well as better impact toughness energies for weld and HAZ with significantly reduced mismatch. It will eventually enable to utilize greater permitted design stresses during fabrication as a result of providing remedies to the common technical and financial issues faced by the conventional wire. The optimum condition of acceptable tensile strength and impact toughness with a lower mechanical mismatching between weld metal and HAZ is achieved by applying suitable (Preheat / PWHT schemes) as well as maintaining adequate interpass / heat input. سلك الحشو الأوستينيتي القائم على النيكل (ERNiCrMo-3) هو الخيار التقليدي لحاويات الغاز الطبيعي المسال المصنوع من صلب 9٪ نيكل باستخدام اللحام القوسي بالمعدن والغاز (GMAW) ، عدم مطابق قوة الشد للمعدن الأساسي يزيد بشكل كبير من تكلفة التصنيع نتيجة لزيادة سماكة الوصلة من أجل الحفاظ علة قوة التحمل بالإضافة إلى كمية كبيرة من سلك الحشو مطلوبة لملء هذه السماكة.
عند استخدام سلك الحشو الفريتي غير التقليدي المطابق للمعدن الأساسي (ERNi11) ، تكون قوة الشد الناتجة أعلى مقارنةً بالمعدن الأساسي بالإضافة إلى متانة أفضل للحام مع تقليل عدم التطابق الميكانيكي بشكل كبير بين اللحام والمنطقة المتأثرة بالحرارة ، مما سيجعل من الممكن في النهاية استخدام ضغوط التصميم الأعلى المسموح بها أثناء التصنيع نتيجة لإيجاد حلول للمشاكل التقنية والاقتصادية المعروفة التي تواجه سلك الحشو الأوستينيتي التقليدي.
يتم تحقيق الحالة المثلى لقوة الشد المقبولة والمتانة مع عدم تطابق ميكانيكي أقل بين اللحام و المنطقة المتأثرة بالحرارة من خلال استخدام (التسخين المسبق المناسب / المعالجة الحرارية المناسبة).
Text in English and abstract in Arabic & English.
Natural gas
9%Ni steel gas metal arc welding Ni-based austenitic filler metal matching ferritic filler metal preheating post weld heat treatment
665.7
Gas metal arc welding of 9%ni steel using non-conventional ferritic welding filler wire for LNG facilities / اللحام القوسي بالمعدن والغاز لصلب 9% نيكل بإستخدام سلك حشو اللحام الفريتي غير التقليدي لحاويات الغاز الطبيعي المسال / by Ahmed Mohamed Abou Al Soud Abd Al Rahman ; Supervisors Prof. M.R.El-Koussy, Prof. Nahed A.Abd El-Raheem, Prof. Waleed A.Khalifa, Prof.A.El-Batahgy. - 102 pages : illustrations ; 30 cm. + CD.
Thesis (Ph.D)-Cairo University, 2024.
Bibliography: pages 97-102.
The facilities which used to store LNG are constructed from nine percent Nickel Steel using GMAW, the conventional/common choice is Nickel-Based consumable (ERNiCrMo-3).Under matching base metal due to strength loss significantly increase the manufacturing cost as a result of increasing the joint thickness in order to retain the strength as well as a significant amount is required for filling the Weldments. When using the non-conventional matching ferritic filler wire (ERNi11), Compared to basic material, the resulting tensile strength is greater, as well as better impact toughness energies for weld and HAZ with significantly reduced mismatch. It will eventually enable to utilize greater permitted design stresses during fabrication as a result of providing remedies to the common technical and financial issues faced by the conventional wire. The optimum condition of acceptable tensile strength and impact toughness with a lower mechanical mismatching between weld metal and HAZ is achieved by applying suitable (Preheat / PWHT schemes) as well as maintaining adequate interpass / heat input. سلك الحشو الأوستينيتي القائم على النيكل (ERNiCrMo-3) هو الخيار التقليدي لحاويات الغاز الطبيعي المسال المصنوع من صلب 9٪ نيكل باستخدام اللحام القوسي بالمعدن والغاز (GMAW) ، عدم مطابق قوة الشد للمعدن الأساسي يزيد بشكل كبير من تكلفة التصنيع نتيجة لزيادة سماكة الوصلة من أجل الحفاظ علة قوة التحمل بالإضافة إلى كمية كبيرة من سلك الحشو مطلوبة لملء هذه السماكة.
عند استخدام سلك الحشو الفريتي غير التقليدي المطابق للمعدن الأساسي (ERNi11) ، تكون قوة الشد الناتجة أعلى مقارنةً بالمعدن الأساسي بالإضافة إلى متانة أفضل للحام مع تقليل عدم التطابق الميكانيكي بشكل كبير بين اللحام والمنطقة المتأثرة بالحرارة ، مما سيجعل من الممكن في النهاية استخدام ضغوط التصميم الأعلى المسموح بها أثناء التصنيع نتيجة لإيجاد حلول للمشاكل التقنية والاقتصادية المعروفة التي تواجه سلك الحشو الأوستينيتي التقليدي.
يتم تحقيق الحالة المثلى لقوة الشد المقبولة والمتانة مع عدم تطابق ميكانيكي أقل بين اللحام و المنطقة المتأثرة بالحرارة من خلال استخدام (التسخين المسبق المناسب / المعالجة الحرارية المناسبة).
Text in English and abstract in Arabic & English.
Natural gas
9%Ni steel gas metal arc welding Ni-based austenitic filler metal matching ferritic filler metal preheating post weld heat treatment
665.7