Evaluation of marginal adaptation of two glass ceramic occlusal veneers under thermocycling : an in vitro study
Sohaila Magdy Mohamed Ali,
Evaluation of marginal adaptation of two glass ceramic occlusal veneers under thermocycling : an in vitro study تقييم التكيف الهامشي لإثنين من قشور الإطباق الخزفية الزجاجية تحت التحمل الحراري : دراسة معملية / by Sohaila Magdy Mohamed Ali ; Supervisors Prof. Badawy Abu El Mahasen Badawy, Dr. Abdelrahman Soliman Badran. - 94 pages : illustrations ; 25 cm. + CD.
Thesis (M.Sc)-Cairo University, 2024.
Bibliography: pages 85-92.
Aim: This study evaluated the marginal adaptation of two glass ceramic occlusal veneers under thermocycling.
Methodology: Eighteen maxillary premolar teeth were prepared to receive occlusal veneer restorations and divided into two main groups according to all ceramic material used ; Group A (n=9) occlusal veneers manufacture from IPS e.max press . Group B (n=9) occlusal veneers manufactured from Vita Ambria with 1.2 mm thickness . The occlusal veneer restorations were cemented to the prepared teeth using dual cured self-adhesive resin cement. The specimens were subjected to thermo-cycling up to 5000 cycles in a thermocycling paths with 50C and 550C. All specimen’s marginal adaptation was measured before and after thermocycling using stereomicroscope .
Results: Regarding the two materials effect, there were non-significant difference between IPS e.max and Vita Ambria on marginal adaptation (P=0.6) . Regarding the thermocycling, there were significant difference in marginal adaptation measurements in IPS e.max and Vita Ambria occlusal veneers before and after thermocycling (P<0.0001).
Conclusion: IPS e.max press and Vita Ambria occlusal veneers with butt joint preparation design can be used in the maxillary premolar region. الغرض من هذه الدراسة المعملية تقييم دقة حواف القشور الخزفية لسطح الاطباق المصنعة من السيرامي الليثيام ديسليكيت ( ايماكس ) مقارنه بالليثوم ديسيليكيت المقوى بالزركونيا (فيتا امبريا ) الملصقه بعد التعرض للتحمل الحرارى .
تم استخدام ثمانية عشر من الاضراس العلوية فى الاسنان فى هذه الدراسة التى تم جمعها من المرضى الذين يعانون من مشاكل اللثة الغير قابلة للمعالجة الخالية من التسوس .
تم تركيب الاسنان فى قوالب من راتنج ايبوكسى لتسهيل توحيد القياسات اثناء تحضير و اختبار لاسنان تم انشاء جهاز مصمم خصيصا للسماح بوضع الاسنان بدقة فى قوالب الراتنج الايبوكسى .
تم تحضير الاسنان لتلقى القشرة الخزفيه لسطح الاطباق 1.2 مم
تم تقسيم الاسنان بشكل عشوائى الى مجموعتين رئيسيتين (9 لكل منهما ) .
المجموعه أ تلتقى القشرة الاطباقية المصنعه من (ايماكس ) فى حين ان المجموعة ب تلتقى قشرة الاطباقية المصنعة من السيراميك المقوى بالزركونيا ( فيتا امبريا ) .
تم تحضير الاسنان لاستقبال القشور الخزفية لسطح الاطباق بستخدام قاطع العمق .
تم تجهيز القشور الخزفية لسطح الطباق للعينات باستخدام تقنية الشمع المفقود و الضغط الحرارى حيث تم ضبط السماكة المطلوبة و كذلك المساحة المتاحه للاصق الكترونيا و بشكل موحد عن طريق استخدام جهاز الكاد كام لخط الشمع .
تم فحص كل القشور الخزفية لوجود اى خلل من الدخل و الخارج .
تم تحضير السطح الداخلى لكل مجموعة طبقاً لتعليمات الشركة المصنعة .
بعد ذلك تم استخدام جهاز تحميل مخصوص لوضع ثقل مقداره 1 كجم بشكل عمودى على العينة اثناء اللصق لضمان الالتصاق التام بين القشرة الخزفية و السطح لاستقبالها .
تم اخضاع جميع العينات للاجهاد الحرارى ل5000 دورة
تم تصوير مسافة الفجوة الهامشية العينة باستخدام مجهر ستيريو بكاميرا مدمجه متصلة بجهاز كمبيوتر شخصى باستخدام تكبير ثابت .
اخذت لقطات من الحواف لكل عينة ثم تم إجراء القياسات المورفوتية لكل لقطة ( 3 نقاط لكل سطح ثم تم جمع البيانات التى تم الحصول عليها و جدولتها ثم اخضاعها للتحليل الاحصائى .
تم الحصول على النتائج التالية :
اظهرت النتايج ان دقة حواف القشرة الاطباقية المصنعة من السيراميك المقوى ( فيتا امبريا ) مساوية لدقة حواف القشرة الاطباقية المصنعة من ايماكس بعد التعرض للاجهاد الحرارى وان الاجهاد الحرارى يؤثر بالسلب على دقة الحواف.
Text in English and abstract in Arabic & English.
Dental implants
Occlusal veneers Press E.max Vita Ambria Butt joint Marginal adaptation Thermocycling
617.69
Evaluation of marginal adaptation of two glass ceramic occlusal veneers under thermocycling : an in vitro study تقييم التكيف الهامشي لإثنين من قشور الإطباق الخزفية الزجاجية تحت التحمل الحراري : دراسة معملية / by Sohaila Magdy Mohamed Ali ; Supervisors Prof. Badawy Abu El Mahasen Badawy, Dr. Abdelrahman Soliman Badran. - 94 pages : illustrations ; 25 cm. + CD.
Thesis (M.Sc)-Cairo University, 2024.
Bibliography: pages 85-92.
Aim: This study evaluated the marginal adaptation of two glass ceramic occlusal veneers under thermocycling.
Methodology: Eighteen maxillary premolar teeth were prepared to receive occlusal veneer restorations and divided into two main groups according to all ceramic material used ; Group A (n=9) occlusal veneers manufacture from IPS e.max press . Group B (n=9) occlusal veneers manufactured from Vita Ambria with 1.2 mm thickness . The occlusal veneer restorations were cemented to the prepared teeth using dual cured self-adhesive resin cement. The specimens were subjected to thermo-cycling up to 5000 cycles in a thermocycling paths with 50C and 550C. All specimen’s marginal adaptation was measured before and after thermocycling using stereomicroscope .
Results: Regarding the two materials effect, there were non-significant difference between IPS e.max and Vita Ambria on marginal adaptation (P=0.6) . Regarding the thermocycling, there were significant difference in marginal adaptation measurements in IPS e.max and Vita Ambria occlusal veneers before and after thermocycling (P<0.0001).
Conclusion: IPS e.max press and Vita Ambria occlusal veneers with butt joint preparation design can be used in the maxillary premolar region. الغرض من هذه الدراسة المعملية تقييم دقة حواف القشور الخزفية لسطح الاطباق المصنعة من السيرامي الليثيام ديسليكيت ( ايماكس ) مقارنه بالليثوم ديسيليكيت المقوى بالزركونيا (فيتا امبريا ) الملصقه بعد التعرض للتحمل الحرارى .
تم استخدام ثمانية عشر من الاضراس العلوية فى الاسنان فى هذه الدراسة التى تم جمعها من المرضى الذين يعانون من مشاكل اللثة الغير قابلة للمعالجة الخالية من التسوس .
تم تركيب الاسنان فى قوالب من راتنج ايبوكسى لتسهيل توحيد القياسات اثناء تحضير و اختبار لاسنان تم انشاء جهاز مصمم خصيصا للسماح بوضع الاسنان بدقة فى قوالب الراتنج الايبوكسى .
تم تحضير الاسنان لتلقى القشرة الخزفيه لسطح الاطباق 1.2 مم
تم تقسيم الاسنان بشكل عشوائى الى مجموعتين رئيسيتين (9 لكل منهما ) .
المجموعه أ تلتقى القشرة الاطباقية المصنعه من (ايماكس ) فى حين ان المجموعة ب تلتقى قشرة الاطباقية المصنعة من السيراميك المقوى بالزركونيا ( فيتا امبريا ) .
تم تحضير الاسنان لاستقبال القشور الخزفية لسطح الاطباق بستخدام قاطع العمق .
تم تجهيز القشور الخزفية لسطح الطباق للعينات باستخدام تقنية الشمع المفقود و الضغط الحرارى حيث تم ضبط السماكة المطلوبة و كذلك المساحة المتاحه للاصق الكترونيا و بشكل موحد عن طريق استخدام جهاز الكاد كام لخط الشمع .
تم فحص كل القشور الخزفية لوجود اى خلل من الدخل و الخارج .
تم تحضير السطح الداخلى لكل مجموعة طبقاً لتعليمات الشركة المصنعة .
بعد ذلك تم استخدام جهاز تحميل مخصوص لوضع ثقل مقداره 1 كجم بشكل عمودى على العينة اثناء اللصق لضمان الالتصاق التام بين القشرة الخزفية و السطح لاستقبالها .
تم اخضاع جميع العينات للاجهاد الحرارى ل5000 دورة
تم تصوير مسافة الفجوة الهامشية العينة باستخدام مجهر ستيريو بكاميرا مدمجه متصلة بجهاز كمبيوتر شخصى باستخدام تكبير ثابت .
اخذت لقطات من الحواف لكل عينة ثم تم إجراء القياسات المورفوتية لكل لقطة ( 3 نقاط لكل سطح ثم تم جمع البيانات التى تم الحصول عليها و جدولتها ثم اخضاعها للتحليل الاحصائى .
تم الحصول على النتائج التالية :
اظهرت النتايج ان دقة حواف القشرة الاطباقية المصنعة من السيراميك المقوى ( فيتا امبريا ) مساوية لدقة حواف القشرة الاطباقية المصنعة من ايماكس بعد التعرض للاجهاد الحرارى وان الاجهاد الحرارى يؤثر بالسلب على دقة الحواف.
Text in English and abstract in Arabic & English.
Dental implants
Occlusal veneers Press E.max Vita Ambria Butt joint Marginal adaptation Thermocycling