Evaluation of fracture resistance of two glass ceramic occlusal veneers under thermocyclic loading : An invitro study /
Huda Ahmad Abdel Hakeem Ibraheem,
Evaluation of fracture resistance of two glass ceramic occlusal veneers under thermocyclic loading : An invitro study / تقييم مقاومة الكسرلاثنين من قشور الاطباق الخزفيه الزجاجيه تحت التحميل الحراري : دراسة معملية / by Huda Ahmad Abdel Hakeem Ibraheem ; Supervisors Prof. Badawy Abu El Mahasen Badawy, Dr. Abdelrahman Soliman Badran. - 94 pages : illustrations ; 25 cm. + CD.
Thesis (M.Sc)-Cairo University, 2024.
Bibliography: pages 85-92.
Aim: This study evaluated the marginal adaptation of two glass ceramic occlusal veneers under thermocycling.
Methodology: Eighteen maxillary premolar teeth were prepared to receive occlusal veneer restorations and divided into two main groups according to all ceramic material used ; Group A (n=9) occlusal veneers manufacture from IPS e.max press . Group B (n=9) occlusal veneers manufactured from Vita Ambria with 1.2 mm thickness . The occlusal veneer restorations were cemented to the prepared teeth using dual cured self-adhesive resin cement. The specimens were subjected to thermo-cycling up to 5000 cycles in a thermocycling paths with 50C and 550C. All specimen’s marginal adaptation was measured before and after thermocycling using stereomicroscope .
Results: Regarding the two materials effect, there were non-significant difference between IPS e.max and Vita Ambria on marginal adaptation (P=0.6) . Regarding the thermocycling, there were significant difference in marginal adaptation measurements in IPS e.max and Vita Ambria occlusal veneers before and after thermocycling (P<0.0001).
Conclusion: IPS e.max press and Vita Ambria occlusal veneers with butt joint preparation design can be used in the maxillary premolar region هذه الدراسة المعملية أجريت لتقييم مقاومة الكسر لقشرة الاطباق المصنوعة من الليثيوم سليكات المقوى بالزركونيا المضغوط مقابل قشرة الأطباق المصنوعة من الليثيوم دايسليكات المضغوط عند تعرضهم للضغط الحراري الدوري .
وقد تم استخدام ثلاثون ضاحكا علويا أول مخلوعا ومن ثم قسمت إلى مجموعتين متساويتين (خمسة عشر لكل مجموعة) وفقا لنوع المادة المستخدمة في صناعة قشور الأطباق.
المجموعة الاولى (أ): قشور الأطباق المصنوعة من مادة الليثيوم دايسليكات المضغوط .
المجموعة الثانيه (ب): التيجان المصنوعة من الليثيوم سليكات المقوى بالزركونيا المضغوط.
تم إجراء تحضير قياسي يبلغ 1.2 مم على السطح الاطباقي لكل الضروس بتصميم اعداد الهامش الحاد باستخدام خط سطح هامش بزاويه 90 درجة.
بعد ذلك تم استخدام التكنولوجيا الرقمية لتصنيع النموذج الشمعي لشكل قشور الأطباق وذلك بعد أخذ صورة لعينة الثلاثين ضرسا بالماسح الضوئي والكاميرا ومن ثم تصنيع النموذج المطلوب وخرطه من الشمع وذلك باستخدام تقنية الكاد كام.
ثم تم ضغط خمسة عشر عينة باستخدام مادة الليثيوم دايسليكات المضغوط وتم ضغط الخمسة عشر الأخرين باستخدام مادة الليثيوم سليكات المقوى بالزيركونيا المضغوط وذلك باتباع الطرق الموصى بها من المصنع ثم تم تلميع وتزجيج قشور الاطباق وفقا لتعليمات المصنع لضمان حصولهم على مستوى أعلى من مقاومة الكسر.
بعد ذلك تم لصق قشور الأطباق على الأضراس المناظرة لها باستخدام لاصق راتنجي ذاتي اللصق ذو علاج مزدوج بعد معالجتها بحمض الهيدروفلوريك والسيالين لضمان قوة التلاصق وذلك باستخدام الجهاز المصمم خصيصا لتوحيد الحمولة الضاغطة على قشور الاطباق خلال فتره اللصق .
تم تعريض كل العينات للتدوير الحراري بمقدار 5000 دوره (تمثل اكلينيكيا 6 أشهر) وذلك لمحاكاة الظروف الاكلينيكيه.
بعد ذلك تم عمل اختبار الكسر للعينات باستخدام (الةاختبار عالمية ) حيث تم الاختباربشكل عمودي على قشور الاطباق.
وبعد اجراء اختبارات مقاومة الكسر للعينات ورصدها تم فحص انواع الكسور الحاصلة للعينات حسب التصنيف الموضوع سابقا.
سجلت الاسنان الضرسية العلوية المعالجة بقشور الاطباق المصنوعة من مادة الليثيوم دايسليكات المضغوط مقاومة للكسر قيمة متوسطة اعلى معنويه احصائيا بالمقارنة مع الضروس العلوية المعالجة بقشور الأطباق المصنوعة من مادة الليثيوم سليكات المقوى بالزيركونيا المضغوط.
وطبقا لانماط وضع الفشل كان الغالب انماط وضع الفشل قابلة للاصلاح في مجموعة ماده الليثيوم دايسليكات المضغوط (86.70%) مع سجل ثانوي لنمط كارثي (13.30%) ، بينما في مجموعة الليثيوم سليكات المقوى بالزيركونيا المضغوط كان النمط الكارثي أعلى من المجموعة الأولى (33.30%) لكن لايزال نمط الكسر القابل للاصلاح أعلى من الكارثي لنفس المجموعة (66.70%).
ضمن حدود هذه الرساله تم التوصل الى ان مقاومة الكسر لقشور الاطباق المصنعه من مادة الليثيوم دايسليكات المضغوط افضل من المصنعه من الليثيوم سيليكات المقوى بالزيركونيا المضغوط.
Text in English and abstract in Arabic & English.
Dental implants
occlusal veneers Lithium disilicate Zirconia reinforced lithium disilicate fracture resistance
617.69
Evaluation of fracture resistance of two glass ceramic occlusal veneers under thermocyclic loading : An invitro study / تقييم مقاومة الكسرلاثنين من قشور الاطباق الخزفيه الزجاجيه تحت التحميل الحراري : دراسة معملية / by Huda Ahmad Abdel Hakeem Ibraheem ; Supervisors Prof. Badawy Abu El Mahasen Badawy, Dr. Abdelrahman Soliman Badran. - 94 pages : illustrations ; 25 cm. + CD.
Thesis (M.Sc)-Cairo University, 2024.
Bibliography: pages 85-92.
Aim: This study evaluated the marginal adaptation of two glass ceramic occlusal veneers under thermocycling.
Methodology: Eighteen maxillary premolar teeth were prepared to receive occlusal veneer restorations and divided into two main groups according to all ceramic material used ; Group A (n=9) occlusal veneers manufacture from IPS e.max press . Group B (n=9) occlusal veneers manufactured from Vita Ambria with 1.2 mm thickness . The occlusal veneer restorations were cemented to the prepared teeth using dual cured self-adhesive resin cement. The specimens were subjected to thermo-cycling up to 5000 cycles in a thermocycling paths with 50C and 550C. All specimen’s marginal adaptation was measured before and after thermocycling using stereomicroscope .
Results: Regarding the two materials effect, there were non-significant difference between IPS e.max and Vita Ambria on marginal adaptation (P=0.6) . Regarding the thermocycling, there were significant difference in marginal adaptation measurements in IPS e.max and Vita Ambria occlusal veneers before and after thermocycling (P<0.0001).
Conclusion: IPS e.max press and Vita Ambria occlusal veneers with butt joint preparation design can be used in the maxillary premolar region هذه الدراسة المعملية أجريت لتقييم مقاومة الكسر لقشرة الاطباق المصنوعة من الليثيوم سليكات المقوى بالزركونيا المضغوط مقابل قشرة الأطباق المصنوعة من الليثيوم دايسليكات المضغوط عند تعرضهم للضغط الحراري الدوري .
وقد تم استخدام ثلاثون ضاحكا علويا أول مخلوعا ومن ثم قسمت إلى مجموعتين متساويتين (خمسة عشر لكل مجموعة) وفقا لنوع المادة المستخدمة في صناعة قشور الأطباق.
المجموعة الاولى (أ): قشور الأطباق المصنوعة من مادة الليثيوم دايسليكات المضغوط .
المجموعة الثانيه (ب): التيجان المصنوعة من الليثيوم سليكات المقوى بالزركونيا المضغوط.
تم إجراء تحضير قياسي يبلغ 1.2 مم على السطح الاطباقي لكل الضروس بتصميم اعداد الهامش الحاد باستخدام خط سطح هامش بزاويه 90 درجة.
بعد ذلك تم استخدام التكنولوجيا الرقمية لتصنيع النموذج الشمعي لشكل قشور الأطباق وذلك بعد أخذ صورة لعينة الثلاثين ضرسا بالماسح الضوئي والكاميرا ومن ثم تصنيع النموذج المطلوب وخرطه من الشمع وذلك باستخدام تقنية الكاد كام.
ثم تم ضغط خمسة عشر عينة باستخدام مادة الليثيوم دايسليكات المضغوط وتم ضغط الخمسة عشر الأخرين باستخدام مادة الليثيوم سليكات المقوى بالزيركونيا المضغوط وذلك باتباع الطرق الموصى بها من المصنع ثم تم تلميع وتزجيج قشور الاطباق وفقا لتعليمات المصنع لضمان حصولهم على مستوى أعلى من مقاومة الكسر.
بعد ذلك تم لصق قشور الأطباق على الأضراس المناظرة لها باستخدام لاصق راتنجي ذاتي اللصق ذو علاج مزدوج بعد معالجتها بحمض الهيدروفلوريك والسيالين لضمان قوة التلاصق وذلك باستخدام الجهاز المصمم خصيصا لتوحيد الحمولة الضاغطة على قشور الاطباق خلال فتره اللصق .
تم تعريض كل العينات للتدوير الحراري بمقدار 5000 دوره (تمثل اكلينيكيا 6 أشهر) وذلك لمحاكاة الظروف الاكلينيكيه.
بعد ذلك تم عمل اختبار الكسر للعينات باستخدام (الةاختبار عالمية ) حيث تم الاختباربشكل عمودي على قشور الاطباق.
وبعد اجراء اختبارات مقاومة الكسر للعينات ورصدها تم فحص انواع الكسور الحاصلة للعينات حسب التصنيف الموضوع سابقا.
سجلت الاسنان الضرسية العلوية المعالجة بقشور الاطباق المصنوعة من مادة الليثيوم دايسليكات المضغوط مقاومة للكسر قيمة متوسطة اعلى معنويه احصائيا بالمقارنة مع الضروس العلوية المعالجة بقشور الأطباق المصنوعة من مادة الليثيوم سليكات المقوى بالزيركونيا المضغوط.
وطبقا لانماط وضع الفشل كان الغالب انماط وضع الفشل قابلة للاصلاح في مجموعة ماده الليثيوم دايسليكات المضغوط (86.70%) مع سجل ثانوي لنمط كارثي (13.30%) ، بينما في مجموعة الليثيوم سليكات المقوى بالزيركونيا المضغوط كان النمط الكارثي أعلى من المجموعة الأولى (33.30%) لكن لايزال نمط الكسر القابل للاصلاح أعلى من الكارثي لنفس المجموعة (66.70%).
ضمن حدود هذه الرساله تم التوصل الى ان مقاومة الكسر لقشور الاطباق المصنعه من مادة الليثيوم دايسليكات المضغوط افضل من المصنعه من الليثيوم سيليكات المقوى بالزيركونيا المضغوط.
Text in English and abstract in Arabic & English.
Dental implants