Effect of novel pre-sintered zirconia surface treatment on shear bond strength between bilayered zirconia and veneering porcelain compared to conventional surface treatments /
Ahmed Atef Sayed Baiomy,
Effect of novel pre-sintered zirconia surface treatment on shear bond strength between bilayered zirconia and veneering porcelain compared to conventional surface treatments / تأثير المعالجة السطحية الجديدة للزركونيا الملبدة مسبقًا على قوة رابطة القص بين الزركونيا ثنائية الطبقات والخزف القشرة مقارنة بالمعالجات السطحية التقليدية : دراسة في المختبر / by Ahmed Atef Sayed Baiomy ; Supervisors Dr. Amina Abdellatif Zaki, Dr. Hanan Ahmed Naguib, Dr. Nourhan Nayef Abd El Halim. - 125 pages : illustrations ; 25 cm. + CD.
Thesis (Ph.D)-Cairo University, 2024.
Bibliography: pages 124-113.
Aim: to evaluate the effect of novel zirconia surface treatment method on shear bond strength between zirconia and veneering porcelain compared to air abrasion and Cojet.
Methods: Twenty-one zirconia discs were fabricated and divided according to surface treatment into three subgroups (n=7), control group I: Air Abrasion, group II: Cojet and group III: Z-etch. Porcelain was built over the zirconia specimens and fired in a ceramic furnace. All specimens were thermocycled and the shear bond strength was tested using a universal testing machine.
Results: A one-way ANOVA test was used to compare between the groups. There was a statistically significant difference between the three groups (P-value = 0.002, Effect size = 0.503) with Z-etch showing the statistically significantly highest mean shear bond strength.
Conclusion: Z-etch is showing promising results in promoting higher bond strength than conventional surface treatment methods. يخضع تطبيق الزركونيا في صناعة طب الأسنان الآن لتوسع كبير، مدعومًا بالعديد من الابتكارات التي تسعى إلى تعزيز خصائص المادة للحصول على الأداء الأمثل في بيئة الفم. أصبحت الزركونيا مادة رئيسية في مجال طب الأسنان الاصطناعي، واكتسبت شعبية باعتبارها مادة لزراعة الأسنان تتنافس بشكل مباشر مع التيتانيوم، والذي يعتبر تقليديا معيارا لإنتاج زراعة الأسنان والمكونات ذات الصلة .
على الرغم من أن الزركونيا تستخدم على نطاق واسع في مجال طب الأسنان، إلا أنها تمتلك العديد من القيود فيما يتعلق بخصائصها التجميلية، والتي تعزى بشكل أساسي إلى مستوى التعتيم العالي. من أجل معالجة هذا القلق، أجرى العلماء تحقيقات في عدة منهجيات، بما في ذلك إجراء تعديلات على تركيبة المادة وتعديلات على كمية أكسيد الإيتريا، بهدف الحصول على أطقم أسنان تمتلك صفات جمالية معززة .
إن اكتشاف تقنية معالجة سطحية مناسبة تكون عملية ويمكن التنبؤ بها، مع ضمان وجود رابطة قوية مقبولة سريريًا بين الزركونيا ثنائية الطبقات وطبقة البورسلين المكسوة، دون المساس بسلامتها الهيكلية، قد شكل باستمرار عقبة كبيرة .
الهدف من هذه الدراسة هو تقييم تأثير ثلاث معالجات سطحية متميزة من الزركونيا على قوة رابطة القص بين الزركونيا والخزف باستخدام طريقة الطبقات النموذجية. بالإضافة إلى ذلك، يهدف هذا البحث إلى تحليل وضع الفشل بين الزركونيا والخزف القشرة بعد اختبار رابطة القص .
Text in English and abstract in Arabic & English.
Prosthodontics
Air-Abrasion Shear bond strength Surface treatment Z-etch Zirconia
617.69
Effect of novel pre-sintered zirconia surface treatment on shear bond strength between bilayered zirconia and veneering porcelain compared to conventional surface treatments / تأثير المعالجة السطحية الجديدة للزركونيا الملبدة مسبقًا على قوة رابطة القص بين الزركونيا ثنائية الطبقات والخزف القشرة مقارنة بالمعالجات السطحية التقليدية : دراسة في المختبر / by Ahmed Atef Sayed Baiomy ; Supervisors Dr. Amina Abdellatif Zaki, Dr. Hanan Ahmed Naguib, Dr. Nourhan Nayef Abd El Halim. - 125 pages : illustrations ; 25 cm. + CD.
Thesis (Ph.D)-Cairo University, 2024.
Bibliography: pages 124-113.
Aim: to evaluate the effect of novel zirconia surface treatment method on shear bond strength between zirconia and veneering porcelain compared to air abrasion and Cojet.
Methods: Twenty-one zirconia discs were fabricated and divided according to surface treatment into three subgroups (n=7), control group I: Air Abrasion, group II: Cojet and group III: Z-etch. Porcelain was built over the zirconia specimens and fired in a ceramic furnace. All specimens were thermocycled and the shear bond strength was tested using a universal testing machine.
Results: A one-way ANOVA test was used to compare between the groups. There was a statistically significant difference between the three groups (P-value = 0.002, Effect size = 0.503) with Z-etch showing the statistically significantly highest mean shear bond strength.
Conclusion: Z-etch is showing promising results in promoting higher bond strength than conventional surface treatment methods. يخضع تطبيق الزركونيا في صناعة طب الأسنان الآن لتوسع كبير، مدعومًا بالعديد من الابتكارات التي تسعى إلى تعزيز خصائص المادة للحصول على الأداء الأمثل في بيئة الفم. أصبحت الزركونيا مادة رئيسية في مجال طب الأسنان الاصطناعي، واكتسبت شعبية باعتبارها مادة لزراعة الأسنان تتنافس بشكل مباشر مع التيتانيوم، والذي يعتبر تقليديا معيارا لإنتاج زراعة الأسنان والمكونات ذات الصلة .
على الرغم من أن الزركونيا تستخدم على نطاق واسع في مجال طب الأسنان، إلا أنها تمتلك العديد من القيود فيما يتعلق بخصائصها التجميلية، والتي تعزى بشكل أساسي إلى مستوى التعتيم العالي. من أجل معالجة هذا القلق، أجرى العلماء تحقيقات في عدة منهجيات، بما في ذلك إجراء تعديلات على تركيبة المادة وتعديلات على كمية أكسيد الإيتريا، بهدف الحصول على أطقم أسنان تمتلك صفات جمالية معززة .
إن اكتشاف تقنية معالجة سطحية مناسبة تكون عملية ويمكن التنبؤ بها، مع ضمان وجود رابطة قوية مقبولة سريريًا بين الزركونيا ثنائية الطبقات وطبقة البورسلين المكسوة، دون المساس بسلامتها الهيكلية، قد شكل باستمرار عقبة كبيرة .
الهدف من هذه الدراسة هو تقييم تأثير ثلاث معالجات سطحية متميزة من الزركونيا على قوة رابطة القص بين الزركونيا والخزف باستخدام طريقة الطبقات النموذجية. بالإضافة إلى ذلك، يهدف هذا البحث إلى تحليل وضع الفشل بين الزركونيا والخزف القشرة بعد اختبار رابطة القص .
Text in English and abstract in Arabic & English.
Prosthodontics
Air-Abrasion Shear bond strength Surface treatment Z-etch Zirconia
617.69