Study of photodegradation of low-density polyethylene composites /
Aya Samir Rizk Ibrahim Ismail,
Study of photodegradation of low-density polyethylene composites / دراسة التحلل الضوئي لمتراكبات البولي إيثيلين منخفض الكثافة by Aya Samir Rizk Ibrahim Ismail ; Supervisors Prof. Dr. Fatma Ashour, Prof. Dr. Mohamed Bassyouni. - 102 pages : illustrations ; 30 cm. + CD.
Thesis (M.Sc)-Cairo University, 2025.
Bibliography: pages 87-102.
This study investigated the photodegradation of low-density polyethylene (LDPE), a major environmental concern due to its accumulation in the environment for many years. Developing photodegradable LDPE with an optimum combination of desirable mechanical properties and photodegradation performance was the main objective of the present study. Ultraviolet radiation accelerated the photodegradation after three months, examining neat LDPE, and LDPE with different additives. These samples were prepared using a twin-screw extruder. Mechanical properties, surface morphology, elemental analysis, thermal stability, physical properties, and chemical characterization were analyzed using different techniques before and after the exposure to UV radiation. Results indicated that adding different additives in LDPE blends enhanced photodegradation compared to neat LDPE, but yield strength decreased. Fourier-transform infrared spectroscopy analysis revealed carbonyl group formation post-UV exposure, confirming polymer photodegradation. Thermal stability and surface hydrophobicity decreased with UV exposure. This research aimed to optimize LDPE formulations for improved photodegradation while maintaining mechanical properties. تبحث هذه الدراسة في التحلل الضوئي للبولي إيثيلين منخفض الكثافة (LDPE)، وهو مصدر قلق بيئي كبير بسبب تراكمه في البيئة لسنوات عديدة. إن تطوير LDPE القابل للتحلل الضوئي مع مزيج مثالي من الخواص الميكانيكية المرغوبة وأداء التحلل الضوئي هو الهدف الرئيسي لهذه الدراسة. أدت الأشعة فوق البنفسجية إلى تسريع عملية التحلل الضوئي بعد ثلاثة أشهر، حيث تم فحص LDPE وLDPE مع إضافات مختلفة. تم تحضير هذه العينات باستخدام جهاز بثق مزدوج اللولب. تم تحليل الخواص الميكانيكية، وتشكل السطح، وتحليل العناصر، والثبات الحراري، والخواص الفيزيائية، والتوصيف الكيميائي باستخدام تقنيات مختلفة قبل وبعد التعرض للأشعة فوق البنفسجية. تشير النتائج إلى أن إضافة إضافات مختلفة في LDPE يمزج التحلل الضوئي المعزز مقارنة بالـ LDPE النقي، ولكن انخفضت قوة الخضوع. كشف التحليل الطيفي للأشعة تحت الحمراء لتحويل فورييه عن تكوين مجموعة الكربونيل بعد التعرض للأشعة فوق البنفسجية، مما يؤكد التحلل الضوئي للبوليمر. انخفض الاستقرار الحراري والكارهة للماء السطحية مع التعرض للأشعة فوق البنفسجية. يهدف هذا البحث إلى تحسين تركيبات LDPE لتحسين التحلل الضوئي مع الحفاظ على الخواص الميكانيكية
Text in English and abstract in Arabic & English.
Chemical Engineering
الهندسة الكيميائية
Photodegradation Low-density Polyethylene Starch Composites UV radiation
660
Study of photodegradation of low-density polyethylene composites / دراسة التحلل الضوئي لمتراكبات البولي إيثيلين منخفض الكثافة by Aya Samir Rizk Ibrahim Ismail ; Supervisors Prof. Dr. Fatma Ashour, Prof. Dr. Mohamed Bassyouni. - 102 pages : illustrations ; 30 cm. + CD.
Thesis (M.Sc)-Cairo University, 2025.
Bibliography: pages 87-102.
This study investigated the photodegradation of low-density polyethylene (LDPE), a major environmental concern due to its accumulation in the environment for many years. Developing photodegradable LDPE with an optimum combination of desirable mechanical properties and photodegradation performance was the main objective of the present study. Ultraviolet radiation accelerated the photodegradation after three months, examining neat LDPE, and LDPE with different additives. These samples were prepared using a twin-screw extruder. Mechanical properties, surface morphology, elemental analysis, thermal stability, physical properties, and chemical characterization were analyzed using different techniques before and after the exposure to UV radiation. Results indicated that adding different additives in LDPE blends enhanced photodegradation compared to neat LDPE, but yield strength decreased. Fourier-transform infrared spectroscopy analysis revealed carbonyl group formation post-UV exposure, confirming polymer photodegradation. Thermal stability and surface hydrophobicity decreased with UV exposure. This research aimed to optimize LDPE formulations for improved photodegradation while maintaining mechanical properties. تبحث هذه الدراسة في التحلل الضوئي للبولي إيثيلين منخفض الكثافة (LDPE)، وهو مصدر قلق بيئي كبير بسبب تراكمه في البيئة لسنوات عديدة. إن تطوير LDPE القابل للتحلل الضوئي مع مزيج مثالي من الخواص الميكانيكية المرغوبة وأداء التحلل الضوئي هو الهدف الرئيسي لهذه الدراسة. أدت الأشعة فوق البنفسجية إلى تسريع عملية التحلل الضوئي بعد ثلاثة أشهر، حيث تم فحص LDPE وLDPE مع إضافات مختلفة. تم تحضير هذه العينات باستخدام جهاز بثق مزدوج اللولب. تم تحليل الخواص الميكانيكية، وتشكل السطح، وتحليل العناصر، والثبات الحراري، والخواص الفيزيائية، والتوصيف الكيميائي باستخدام تقنيات مختلفة قبل وبعد التعرض للأشعة فوق البنفسجية. تشير النتائج إلى أن إضافة إضافات مختلفة في LDPE يمزج التحلل الضوئي المعزز مقارنة بالـ LDPE النقي، ولكن انخفضت قوة الخضوع. كشف التحليل الطيفي للأشعة تحت الحمراء لتحويل فورييه عن تكوين مجموعة الكربونيل بعد التعرض للأشعة فوق البنفسجية، مما يؤكد التحلل الضوئي للبوليمر. انخفض الاستقرار الحراري والكارهة للماء السطحية مع التعرض للأشعة فوق البنفسجية. يهدف هذا البحث إلى تحسين تركيبات LDPE لتحسين التحلل الضوئي مع الحفاظ على الخواص الميكانيكية
Text in English and abstract in Arabic & English.
Chemical Engineering
الهندسة الكيميائية
Photodegradation Low-density Polyethylene Starch Composites UV radiation
660