Evaluation of surface roughness and marginal microleakage of zirconia reinforced glass ionomer (zirconomer) versus resin modified glass ionomer in class v restoration in primary molars : in vitro study /
Hala Ahmed Al Tijani Ibrahim,
Evaluation of surface roughness and marginal microleakage of zirconia reinforced glass ionomer (zirconomer) versus resin modified glass ionomer in class v restoration in primary molars : in vitro study / تقييم مدى الخشونة والتسرب الدقيق الهامشي في الحشوات الزجاجية المدعمة بالزيركون مقابل الحشوات الزجاجية الصمغية في الأسنان اللبنية : دراسة معملية by Hala Ahmed Al Tijani Ibrahim ; Supervisors Prof. Dr. Sherine Ezz El Din, Dr. Nouran Mamdouh. - 84 pages : illustrations ; 25 cm. + CD.
Thesis (Ph.D)-Cairo University, 2023.
Bibliography: pages 72-81.
Aim: To evaluate surface roughness and marginal microleakage of Zirconia Reinforced Glass Ionomer (Zirconomer) versus Resin modified Glass Ionomer (Riva Light Cure) in restoring class V cavities in primary molars.
Methodology: Thirty-eight primary molars were divided into two groups, group 1 for Zirconomer and group 2 for Riva LC. Class V cavities were prepared on all molars and restored with their assigned restorative material. For microleakage evaluation, teeth were subjected to thermocycling, immersed in methylene blue dye and sectioned buccolingually. Assessment of the degree of dye penetration was done under stereomicroscope. For surface roughness, molars were subjected to toothbrushing using an automated brushing simulator, a before and after surface roughness measurements were recorded using atomic force microscope. An Independent t test was performed for surface roughness and Chi square test for microleakage evaluation.
Result: Zirconomer showed lower surface roughness values before and after simulated toothbrushing than Riva LC. Both materials showed microleakage with a higher mean score for Zirconomer group than Riva LC group.
Conclusion: Within the limitation of the study, Zirconomer showed lower surface roughness values than Riva LC, but higher microleakage values. تسوس الأسنان عند الأطفال هو مرض شائع بمعدل تطور سريع. يسمح الاكتشاف المبكر للتسوس بعلاج أكثر تحفظا ووقائية بينما يتطلب التسوس المتقدم طرقا أكثر توغلا. تتوفر العديد من خيارات المواد لترميم الأسنان اللبنية، اكتسبت مادة الأسمنت الأيوني الزجاجي شعبيتها في طب أسنان الأطفال نظرا لأن المادة أقل حساسية للتقنية المتبعة لوضعها وتتطلب وقتا أقل مع خصائص التوافق الحيوي والنشاط المضاد للبكتيريا وإطلاق الفلورايد والترابط الكيميائي للمينا والعاج.
تم إجراء تعديلات متعددة على المادة للتغلب على بعض عيوبها مثل الخصائص الميكانيكية الرديئة والحساسية للرطبوبة. أحد هذه التعديلات هو الأيونومر الزجاجي المعدل بالصمغ ، والذي أصبح خيارا مفضلا لترميم الأسنان الأولية .تعديل آخر أحدث هو أيونومر الزجاج المعدل بزيركون.
تعد متانة المادة الترميمية عامل مهما يجب مراعاته عند اتخاذ قرار بشأن المادة الترميمية المستخدمة لعلاج التسوس لدى الأطفال. يمكن تحقيق المتانة بشكل أساسي من خلال وجود التصاق قوي للمادة بسطح السن لمنع الإزاحة والتسرب حول هامشها ، مما قد يؤدي في النهاية إلى تكوين تسوس ثانوي. علاوة على ذلك ، فإن القدرة على التحكم في تضاريس سطح المادة الترميمة لمنع تراكم اللويحة السنية الذي يعد أحد الأسباب الرئيسية لتكوين التسوس هو عامل مهم آخر ، وكلها تؤثر على قرار المادة الترميمة المناسبة.
هذه الدراسة المعملية تهدف إلى تقييم مدى خشونة السطح والتسرب الدقيق الهامشي في الحشوات الزجاجية المدعمة بالزيركون ((zirconomer مقابل الحشوات الزجاجية الصمغية (Riva Light Cure) في الأضراس اللبنية.
الطرق والمواد: تم جمع 38 ضرساً لبنياً ثانوياً وتقسيمها عشوائياً إلى مجموعتين (1 و 2 ) ، المجموعة 1 تمثل مادة ال((zirconomer والمجموعة 2 تمثل مادة (Riva Light Cure) . كل مجموعة تم تقسيمها الى مجموعتين فرعيتين ، المجموعة a1 و 2a تحتوي كل واحدة منهما على 12 ضرساً من أجل اختبار التسرب الدقيق الهامشي. المجموعتان الفرعيتان 1b و 2b تحتوي كل واحدة منهما على 7 اضراس من أجل إختبار خشونة سطح المواد. تم تحضير تجويف من النوع الخامس بقياسات متساوية على سطح الاضراس (class V) وترميمها بالحشوة المقررة لكل مجموعة. لتقييم التسرب الدقيق الهامشي ، تم تعريض الاسنان لدورات حرارية 250 دورة ،بعد ذلك وضعت الأسنان في صبغة زرقاء لمدة 24 ساعة (methylene blue) ، بعد ذلك تم غسلها وتجفيفها وتقطيعها الى انصاف وفحصها تحت المجهر (stereomicroscope) لتحديد درجة تسرب الصبغة. فيما يخص تقييم مدى خشونة سطح الحشوات ، تم تعريض الحشوات لمحاكة لعملية تفريش الأسنان بالفرشاة والمعجون بإستخدام جهاز ألي، تم قياس خشونة سطح الأسنان قبل وبعد عملية تفريش الاسنان . تم استخدام An Independent t test لمقارنة اختلاف خشونة سطح الحشوات قبل وبعد عملية محاكة تفريش الأسنان، و تم استخدام Chi square test في تقييم التسرب الرقيق الهامشي.
النتائج: أظهرت نتائج الدراسة الحالية أن Zirconomer أعطى قراءات أقل لخشونة سطح الحشوات قبل وبعد محاكة تقريش الأسنان بالمقارنة مع Riva LC. فيما يخص التسرب الدقيق الهامشي أظهرت المادتين قيم تسرب بي مقادير مختلفة لكن متوسط قيم قرائات zirconomer كانت أعلى من القرائات المسجلة لي Riva LC
Text in English and abstract in Arabic & English.
Pediatric Dentistry
طب أسنان الأطفال
Zirconia reinforced glass ionomer Zirconomer Resin modified glass ionomer Riva Light Cure; Surface roughness; Microleakage class V primary molars.
617.645
Evaluation of surface roughness and marginal microleakage of zirconia reinforced glass ionomer (zirconomer) versus resin modified glass ionomer in class v restoration in primary molars : in vitro study / تقييم مدى الخشونة والتسرب الدقيق الهامشي في الحشوات الزجاجية المدعمة بالزيركون مقابل الحشوات الزجاجية الصمغية في الأسنان اللبنية : دراسة معملية by Hala Ahmed Al Tijani Ibrahim ; Supervisors Prof. Dr. Sherine Ezz El Din, Dr. Nouran Mamdouh. - 84 pages : illustrations ; 25 cm. + CD.
Thesis (Ph.D)-Cairo University, 2023.
Bibliography: pages 72-81.
Aim: To evaluate surface roughness and marginal microleakage of Zirconia Reinforced Glass Ionomer (Zirconomer) versus Resin modified Glass Ionomer (Riva Light Cure) in restoring class V cavities in primary molars.
Methodology: Thirty-eight primary molars were divided into two groups, group 1 for Zirconomer and group 2 for Riva LC. Class V cavities were prepared on all molars and restored with their assigned restorative material. For microleakage evaluation, teeth were subjected to thermocycling, immersed in methylene blue dye and sectioned buccolingually. Assessment of the degree of dye penetration was done under stereomicroscope. For surface roughness, molars were subjected to toothbrushing using an automated brushing simulator, a before and after surface roughness measurements were recorded using atomic force microscope. An Independent t test was performed for surface roughness and Chi square test for microleakage evaluation.
Result: Zirconomer showed lower surface roughness values before and after simulated toothbrushing than Riva LC. Both materials showed microleakage with a higher mean score for Zirconomer group than Riva LC group.
Conclusion: Within the limitation of the study, Zirconomer showed lower surface roughness values than Riva LC, but higher microleakage values. تسوس الأسنان عند الأطفال هو مرض شائع بمعدل تطور سريع. يسمح الاكتشاف المبكر للتسوس بعلاج أكثر تحفظا ووقائية بينما يتطلب التسوس المتقدم طرقا أكثر توغلا. تتوفر العديد من خيارات المواد لترميم الأسنان اللبنية، اكتسبت مادة الأسمنت الأيوني الزجاجي شعبيتها في طب أسنان الأطفال نظرا لأن المادة أقل حساسية للتقنية المتبعة لوضعها وتتطلب وقتا أقل مع خصائص التوافق الحيوي والنشاط المضاد للبكتيريا وإطلاق الفلورايد والترابط الكيميائي للمينا والعاج.
تم إجراء تعديلات متعددة على المادة للتغلب على بعض عيوبها مثل الخصائص الميكانيكية الرديئة والحساسية للرطبوبة. أحد هذه التعديلات هو الأيونومر الزجاجي المعدل بالصمغ ، والذي أصبح خيارا مفضلا لترميم الأسنان الأولية .تعديل آخر أحدث هو أيونومر الزجاج المعدل بزيركون.
تعد متانة المادة الترميمية عامل مهما يجب مراعاته عند اتخاذ قرار بشأن المادة الترميمية المستخدمة لعلاج التسوس لدى الأطفال. يمكن تحقيق المتانة بشكل أساسي من خلال وجود التصاق قوي للمادة بسطح السن لمنع الإزاحة والتسرب حول هامشها ، مما قد يؤدي في النهاية إلى تكوين تسوس ثانوي. علاوة على ذلك ، فإن القدرة على التحكم في تضاريس سطح المادة الترميمة لمنع تراكم اللويحة السنية الذي يعد أحد الأسباب الرئيسية لتكوين التسوس هو عامل مهم آخر ، وكلها تؤثر على قرار المادة الترميمة المناسبة.
هذه الدراسة المعملية تهدف إلى تقييم مدى خشونة السطح والتسرب الدقيق الهامشي في الحشوات الزجاجية المدعمة بالزيركون ((zirconomer مقابل الحشوات الزجاجية الصمغية (Riva Light Cure) في الأضراس اللبنية.
الطرق والمواد: تم جمع 38 ضرساً لبنياً ثانوياً وتقسيمها عشوائياً إلى مجموعتين (1 و 2 ) ، المجموعة 1 تمثل مادة ال((zirconomer والمجموعة 2 تمثل مادة (Riva Light Cure) . كل مجموعة تم تقسيمها الى مجموعتين فرعيتين ، المجموعة a1 و 2a تحتوي كل واحدة منهما على 12 ضرساً من أجل اختبار التسرب الدقيق الهامشي. المجموعتان الفرعيتان 1b و 2b تحتوي كل واحدة منهما على 7 اضراس من أجل إختبار خشونة سطح المواد. تم تحضير تجويف من النوع الخامس بقياسات متساوية على سطح الاضراس (class V) وترميمها بالحشوة المقررة لكل مجموعة. لتقييم التسرب الدقيق الهامشي ، تم تعريض الاسنان لدورات حرارية 250 دورة ،بعد ذلك وضعت الأسنان في صبغة زرقاء لمدة 24 ساعة (methylene blue) ، بعد ذلك تم غسلها وتجفيفها وتقطيعها الى انصاف وفحصها تحت المجهر (stereomicroscope) لتحديد درجة تسرب الصبغة. فيما يخص تقييم مدى خشونة سطح الحشوات ، تم تعريض الحشوات لمحاكة لعملية تفريش الأسنان بالفرشاة والمعجون بإستخدام جهاز ألي، تم قياس خشونة سطح الأسنان قبل وبعد عملية تفريش الاسنان . تم استخدام An Independent t test لمقارنة اختلاف خشونة سطح الحشوات قبل وبعد عملية محاكة تفريش الأسنان، و تم استخدام Chi square test في تقييم التسرب الرقيق الهامشي.
النتائج: أظهرت نتائج الدراسة الحالية أن Zirconomer أعطى قراءات أقل لخشونة سطح الحشوات قبل وبعد محاكة تقريش الأسنان بالمقارنة مع Riva LC. فيما يخص التسرب الدقيق الهامشي أظهرت المادتين قيم تسرب بي مقادير مختلفة لكن متوسط قيم قرائات zirconomer كانت أعلى من القرائات المسجلة لي Riva LC
Text in English and abstract in Arabic & English.
Pediatric Dentistry
طب أسنان الأطفال
Zirconia reinforced glass ionomer Zirconomer Resin modified glass ionomer Riva Light Cure; Surface roughness; Microleakage class V primary molars.
617.645