Biophysical studies on bone cement composites based on polyester fumarate /
Nagwa Ahmed Kamel Ahmed
Biophysical studies on bone cement composites based on polyester fumarate / دراسة الخواص البيوفيزيائية لمتراكبات اسمنت العظام التى تعتمد فى تركيبها على البولى استر فيوماريت Nagwa Ahmed Kamel Ahmed ; Supervised Wafaa Mohamed Ahmed Khalil , Mohamed Karam Elsayed Zabady , Kamal Nasr Abdelnour - Cairo : Nagwa Ahmed Kamel Ahmed , 2013 - 136 P. : charts , facsimiles ; 25cm
Thesis (Ph.D.) - Cairo University - Faculty of Science - Department of Biophysics
Polyproplene fumarate (PPF) as unsaturated polyester was prepared and characterized by means of ¹HNMR, FTIR and GPC. The investigated polyster was crosslinked with N-viny1 pyrrolidone (NVP), methy1 methacrylate (MMA) and a mixture of NVP and MMA (1:1 weight ratio) and filled with gypsum with concentrations (60, 65, and 70 wt %)
Calcium sulphate dihydrate Hydroxyapatite Poly (propylene fumarate)
Biophysical studies on bone cement composites based on polyester fumarate / دراسة الخواص البيوفيزيائية لمتراكبات اسمنت العظام التى تعتمد فى تركيبها على البولى استر فيوماريت Nagwa Ahmed Kamel Ahmed ; Supervised Wafaa Mohamed Ahmed Khalil , Mohamed Karam Elsayed Zabady , Kamal Nasr Abdelnour - Cairo : Nagwa Ahmed Kamel Ahmed , 2013 - 136 P. : charts , facsimiles ; 25cm
Thesis (Ph.D.) - Cairo University - Faculty of Science - Department of Biophysics
Polyproplene fumarate (PPF) as unsaturated polyester was prepared and characterized by means of ¹HNMR, FTIR and GPC. The investigated polyster was crosslinked with N-viny1 pyrrolidone (NVP), methy1 methacrylate (MMA) and a mixture of NVP and MMA (1:1 weight ratio) and filled with gypsum with concentrations (60, 65, and 70 wt %)
Calcium sulphate dihydrate Hydroxyapatite Poly (propylene fumarate)