Investigation of copper matrix by powder metallurgy technology for the manufacture of brake pads /
Alshaimaa Ahmed Mohammed Ali
Investigation of copper matrix by powder metallurgy technology for the manufacture of brake pads / دراسة المواد المركبة من النحاس لتصنيع لقم الفرامل Alshaimaa Ahmed Mohammed Ali ; Supervised Abdelhalim Mohamed Abdelhalim , Omayma Abdelgawad Elkady - Cairo : Alshaimaa Ahmed Mohammed Ali , 2020 - 110 P . : charts , facsmilies , photographs ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Mechanical Design and Production
This investigation pays attention to Cu-composite, which is formed from Cu matrix reinforced with graphite and iron. To demonstrate efficiency and increase the life time of copper matrix for brake pads, the graphite is to be added to Cu matrix with different amounts that are 0, 2, 6, and 12 wt. %. Microstructure by SEM, morphology XRD analysis, relative density, hardness, wear resistance and CTE of the sintered composites were investigated. The results show that the best relative density is 6wt. %Gr (97.31%) with hardness 105.3HV. The compressive strength increases with increasing graphite to 6%, and it decreases with increasing graphite by 12% in Cu matrix. The wear weight loss of S3,S4 and S5 specimens decreases with increasing graphite in Cu matrix. CTE decreases by increasing graphite to 6wt.%
Brake Pads Cu-Matrix Graphite
Investigation of copper matrix by powder metallurgy technology for the manufacture of brake pads / دراسة المواد المركبة من النحاس لتصنيع لقم الفرامل Alshaimaa Ahmed Mohammed Ali ; Supervised Abdelhalim Mohamed Abdelhalim , Omayma Abdelgawad Elkady - Cairo : Alshaimaa Ahmed Mohammed Ali , 2020 - 110 P . : charts , facsmilies , photographs ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Mechanical Design and Production
This investigation pays attention to Cu-composite, which is formed from Cu matrix reinforced with graphite and iron. To demonstrate efficiency and increase the life time of copper matrix for brake pads, the graphite is to be added to Cu matrix with different amounts that are 0, 2, 6, and 12 wt. %. Microstructure by SEM, morphology XRD analysis, relative density, hardness, wear resistance and CTE of the sintered composites were investigated. The results show that the best relative density is 6wt. %Gr (97.31%) with hardness 105.3HV. The compressive strength increases with increasing graphite to 6%, and it decreases with increasing graphite by 12% in Cu matrix. The wear weight loss of S3,S4 and S5 specimens decreases with increasing graphite in Cu matrix. CTE decreases by increasing graphite to 6wt.%
Brake Pads Cu-Matrix Graphite