Thesis (M.Sc)-Cairo University, 2025.

Bibliography: pages 88-96.

This research examines the pull-out behavior of slag-based geopolymer mortars,
focusing on how interfacial bond strength is influenced by key parameters such as
silicate modulus (Ms), activator-to-binder ratio (A/B), fiber type, and fiber
orientation. Unlike studies aiming to enhance mortar strength through fiber
reinforcement, this work isolates the fiber–matrix interaction to understand how
chemical composition and mechanical variables affect bond performance.
Experimental testing includes compressive strength, direct tension, and pull-out
tests on dog-bone specimens using single hooked and corrugated steel fibers at
various angles. The outcomes aim to clarify how Ms and A/B ratios govern
geopolymerization and fiber anchorage, providing insights for optimizing
interfacial behavior in eco-friendly, alkali-activated composites.

يبحث هذا العمل في سلوك السحب (Pull-out) للمونة الجيوبوليميرية المعتمدة على خبث الأفران الحبيبي المطحون (GGBFS)، مع التركيز على تأثير مقاومة التماسك البيني الناتجة عن تغير معامل السيليكات (Ms)، ونسبة المنشط إلى الرابط (A/B)، ونوع الألياف واتجاهها. يهدف البحث إلى دراسة التفاعل بين الألياف والمصفوفة بعيدًا عن تعزيز مقاومة المونة الكلية. تضمن البرنامج التجريبي اختبارات الضغط، والشد المباشر، والسحب باستخدام عينات على شكل عظم الكلب مزودة بألياف فولاذية بخطاف منفرد ومتموجة بزوايا مختلفة. وتوضح النتائج أثر التركيب الكيميائي والمتغيرات الميكانيكية على كفاءة التماسك في المواد القلوية المفعّلة الصديقة للبيئة