Manufacturing of alumina - zirconia composites for biomedical applications by ceramic injection molding / Mohammed Ayman Abuelezz ; Supervised Rainer Gadow , Frank Kern , Mahmoud Zawrah
Material type:
TextLanguage: English Publication details: Cairo : Mohammed Ayman Abuelezz , 2009Description: 59 Leaves : charts K facsimiles ; 30cmOnline resources: Dissertation note: Thesis (M.Sc.) - German University - Faculty of Postgraduate Studies and Scientific Research - Department of Materials Engineering Summary: Zirconia toughened alumina (ZTA) are nowadays becoming an alternative to common metal biomedical components . Anear - net - shape process is achieved by the successful injection molding of ZTA at varying yttria contents . The ZTA feedstocks were homogenized and the rheological behavior was investigated to optimize the mold filling process during injection molding
| Item type | Current library | Home library | Call number | Status | Barcode | |
|---|---|---|---|---|---|---|
Thesis
|
قاعة الثقاقات الاجنبية - الدور الثالث | المكتبة المركزبة الجديدة - جامعة القاهرة | Cai01.34.M.Sc.2009.Mo.M (Browse shelf(Opens below)) | Not for loan | 01010110052243000 |
Browsing المكتبة المركزبة الجديدة - جامعة القاهرة shelves Close shelf browser (Hides shelf browser)
Thesis (M.Sc.) - German University - Faculty of Postgraduate Studies and Scientific Research - Department of Materials Engineering
Zirconia toughened alumina (ZTA) are nowadays becoming an alternative to common metal biomedical components . Anear - net - shape process is achieved by the successful injection molding of ZTA at varying yttria contents . The ZTA feedstocks were homogenized and the rheological behavior was investigated to optimize the mold filling process during injection molding