TY  - GEN
AU  - Sobhy Abd El Hameed Mahgob
AU  - Hafez Abd El azeem Ahmed , 
AU  - Kamal Elmenshawy Mohamed , 
AU  - Randa Mohamed Abd El Karim , 
TI  - Effect of nitrogen content on corrosive wear of 316 L austenitic stainless steel / 
PY  - 2005///
CY  - Cairo : 
PB  - Sobhy Abd El Hameed Mahgob , 
KW  - nitrogen
KW  - Potentiodynamic
KW  - stainless steel
N1  - Thesis (M.Sc.) - Cairo University - Faculty Of Engineering - Department Of Metallurgical Engineering; Issued also as CD
N2  - Microstructure examination of as received , solution and aging heat treated specimens was conducted by electron and optical microscopy before and after corrosionThe results showed that , there is no precipitate of nitride in as received or solution heat treated samplesOn the other hand by increasingging temperature there are precipitates of nitrideAlso the examination illustrated that , the tendency of abrasion is decreased by increasing nitrogen content in as received and solution heat treated this due to nitrogen had been completely dissolved in solution heat treatment conditions and hence improves their wear resistance
UR  - http://172.23.153.220/th.pdf
ER  -