000			09388namaa22004331i 4500
003			EG-GICUC
005			20260119115731.0
008			260103s2025 ua a|||frm||| 000 0 eng d
040			_aEG-GICUC _beng _cEG-GICUC _dEG-GICUC _erda
041	0		_aeng _beng _bara
049			_aDeposit
082	0	4	_a571.4
092			_a571.4 _221
097			_aPh.D
099			_aCai01.12.04.Ph.D.2025.Fa.P
100	0		_aFatma Mahmoud Mohamed Yassin, _epreparation.
245	1	0	_aPreparation of composite nanomaterials for biosensing applications / _cby Fatma Mahmoud Mohamed Yassin ; Supervision Dr. Heba Mohamed Fahmy, Dr. Mohamed Mahmoud Fathy.
246	1	5	_aتحضير الجسيمات النانومترية المركبة لتطبيقات الاستشعار الحيوي
264		0	_c2025.
300			_a95 pages : _billustrations ; _c25 cm. + _eCD.
336			_atext _2rda content
337			_aUnmediated _2rdamedia
338			_avolume _2rdacarrier
502			_aThesis (Ph.D)-Cairo University, 2025.
504			_aBibliography: pages 70-95.
520		3	_aNanotechnology is an important area of science that concentrates on developing tiny particles with distinct properties ranging from 10 to 1000 nm in size. These particles exhibit different mechanical, chemical, and physical characteristics than larger bulk molecules. Iron oxide nanoparticles (IO-NPs), with their intrinsic peroxidase-like efficacy, are crucial in synthesizing artificial nanozymes. Novel IO-NPs-based nanozymes were synthesized in this study to serve as peroxidase (POD) mimic enzymes. The formation of well-dispersed nanozymes with large surface areas and high porosities is achieved via modification of IO-NPs with a Chitosan- dextran sulfate (CD) matrix (IO-CD NPs) using different molecular weights (MW) of Chitosan (low, medium, and high) for the preparation of IO-LCD NPs, IO-MCD NPs, and IO-HCD NPs, respectively. The physical properties of IO-NPs and IO-CDS NPs were assessed through biophysical characterizing techniques, including transmission electron microscopy (TEM), dynamic light scattering (DLS), atomic force microscopy (AFM), gas isotherm (N2-isotherm), scanning electron microscope (SEM), energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), vibrating sample magnetometer (VSM), and X-ray photoelectron spectroscopy (XPS). The results revealed that IO-CD NPs had a spherical shape with different texture properties. The synthesized IO-CD NPs nanocomposites were found to have moderate stability. From EDX results, the weight percentage of Fe in IO- CD NPs decreased as the MW of Chitosan increased. The weight percentage of Fe was found to be 18.25±12.91, 16.71±7.12, and 14.69±7.85% for IO-LCD NPs, IO-MCD NPs, and IO-HCD NPs, respectively. The S-shaped hysteresis loops with high saturation magnetization (Ms) and low remanent magnetization (Mr) and coercivity (Hc) values show that IO-CD NPs nanocomposites exhibit superparamagnetic behavior. Gas Isotherm results revealed that IO-LCD NPs had a large specific surface area (69.43 m²/g), a large pore diameter (3.56 nm), and a most significant pore volume (0.06 cc/g) compared to other prepared nanocomposites. IO-MCD NPs had a specific surface area (25.70 m²/g), pore diameter (3.33 nm), and pore volume (0.03 cc/g). IO-HCD NPs had a specific surface area (41.54 m²/g), pore diameter (3.11 nm), and pore volume (0.05 cc/g). For prepared nanozymes, steady-state kinetics was used to calculate the kinetic parameters: Michaelis-Menten constant (Km) and the maximum reaction velocity (Vmax). Through the catalytic oxidation of a peroxidase substrate, 3,3,5,5′- tetramethylbenzidine (TMB), in the presence of hydrogen peroxide (H2O2), prepared nanocomposites demonstrated a notable degree of peroxidase activity. IO-CDS NPs had a stronger affinity for H2O2 and TMB, as the determined Michaelis-Menton constant (Km) revealed. Interestingly, it was found that the nanocomposite formed using low molecular weight Chitosan (IO-LCD NPs) has the highest affinity to the substrate (H2O2) and higher peroxidase-like activity with a Km value (0.017 mM) and maximum reaction velocity (Vmax = 2.14 × 10−7 M s−1). The texture properties of IO-LCD NPs and their affinity to H2O2 and TMB substrates made them the best choice for use as nanozymes for different applications. Colorimetric glucose detection using IO-CD NPs was employed as a sensor to measure glucose quantitatively in the presence of glucose oxidase (Gox). IO-LCD NPs exhibit the lowest value of the limit of detection (LOD) at 4.48 µM, which revealed that it was more selective and sensitive for glucose detection in a linear range from 0.05 µM to 0.25 µM. This selectivity, specificity, peroxidase-like activity, and texture properties, such as large surface area and porosity of IO-LCD NPs, made it the best choice for colorimetric glucose detection in the biomedical field
520		3	_aجسيمات أكسيد الحديد النانوية (IO-NPs) تتمتع بخصائص إنزيمات صناعية (نانوزيم) تشبه خصائص الإنزيمات الطبيعية، مثل الخصائص البيروكسيدية لإنزيم. (HRP) لذلك، اكتسبت جسيمات أكسيد الحديد أهمية واسعة في تصنيع مركبات نانوية ذات خصائص إنزيمية. تحظى الجسيمات النانوية التي تمتلك خصائص بعض الإنزيمات الطبيعية باهتمام كبير نظراً لعدة أسباب، منها هياكلها القابلة للتعديل، وتركيباتها الكيميائية، بالإضافة إلى التكلفة المنخفضة، والثبات العالي، وسهولة التحضير، والخصائص الفائقة. الهدف من العمل المقدم هو تصنيع جسيمات نانوية باستخدام جسيمات أكسيد الحديد النانوية المدعمة بمركب كبريتات دكسترين الكيتوزان (IO-CD NPs)، باستخدام أوزان جزيئية مختلفة من الكيتوزان (منخفضة، ومتوسطة، وعالية)، لإعداد جسيمات نانو IO-LCD NPs، وجسيمات نانو IO-MCD NPs، وجسيمات نانو IO-HCD NPs، على التوالي. تم تقييم الخصائص من خلال تقنيات التوصيف البيوفيزيائي مثل المجهر الإلكتروني النافذ (TEM)، والتشتت الضوئي الديناميكي (DLS)، والفحص المجهري بالقوة الذرية (AFM)، والمجهر الإلكتروني الماسح (SEM)، والتحليل الطيفي للأشعة السينية المشتتة للطاقة (EDX)، والحيود بالأشعة السينية (XRD)، ومقياس المغناطيسية للعينة المهتزة (VSM)، والتحليل الطيفي للفوتون الإلكتروني بالأشعة السينية (XPS). أظهرت النتائج أن هذه الجسيمات النانوية تتمتع بخصائص مغناطيسية فائقة، بالإضافة إلى خصائص إنزيمية عالية. كما أنها تُظهر استقرارًا ممتازًا في الظروف القاسية، ويمكنها توفير العديد من المواقع النشطة على سطحها لتحسين النشاط الكلي لها كإنزيمات مصنعة. أظهرت الجسيمات النانوية المحضرة نشاطًا عاليًا يشبه نشاط إنزيم البيروكسيديز في وجود H₂O₂ وTMB. بعد ذلك، تم استخدام جزيئات IO-CD النانوية للكشف عن الجلوكوز باستخدام القياسات اللونية (Colorimetric Detection). تُستخدم هذه الجسيمات النانوية كمستشعرات لقياس الجلوكوز كميًا بالتعاون مع أوكسيديز الجلوكوز (Gox) . وقد أظهرت جميع العينات انتقائية قوية للكشف عن الجلوكوز. وكشفت المقارنة بين العينات الثلاث أن جزيئات IO-LCD النانوية تتمتع بأدنى حد للكشف (LOD)، مما يشير إلى حساسية وانتقائية أكبر للكشف عن الجلوكوز. وبفضل الجمع بين هذه الانتقائية والنشاط الشبيه بالبيروكسيديز، تُعد جزيئات IO-CD النانوية الخيار الأفضل للكشف عن الجلوكوز باستخدام القياسات اللونية في المجال الطبي الحيوي.
530			_aIssues also as CD.
546			_aText in English and abstract in Arabic & English.
650		0	_aBiophysics
650		0	_aالفيزياء الحيوية
653		1	_airon oxide _ananozyme _aChitosan _aperoxidase mimic _adextran sulfate _aglucose _acolorimetric detection _aأكسيد الحديد _aكيتوزان
700	0		_aHeba Mohamed Fahmy _ethesis advisor.
700	0		_aMohamed Mahmoud Fathy _ethesis advisor.
900			_b01-01-2025 _cHeba Mohamed Fahmy _cMohamed Mahmoud Fathy _UCairo University _FFaculty of Science _DDepartment of Biophysics
905			_aShimaa _eEman Ghareb
942			_2ddc _cTH _e21 _n0
999			_c177340