Effect of Heat Treatment and Alloying Elements on Microstructure and Mechanical Properties of Cold Work Shock Resisting Tool Steel / By Mahmoud Ahmed Essam Mohammed Abdelrheem; Under the Supervision of Prof.Dr. Hassan Megahed, Prof.Dr. Emad EL-Kashif, Prof.Dr. Ahmed Y. Shash, Prof.Dr. Mohamed Kamal El Fawakhry

By:

Mahmoud Ahmed Essam Mohammed Abdelrheem [preparation.]

Contributor(s):

Material type: Text

TextLanguage: English Summary language: English, Arabic Producer: 2023Description: 117 pages : illustrations ; 30 cm. + CDContent type:

text

Media type:

Unmediated

Carrier type:

volume

Other title:

تأثير المعاملات الحرارية والعناصر السبائكية على البنية المجهرية والخواص الميكانيكية لصلب العدةالمقاوم للصدمات المستخدم في التشكيل على البارد [Added title page title]

Subject(s):

DDC classification:

621.564

Available additional physical forms:

Issued also as CD

Dissertation note: Thesis (Ph.D)-Cairo University, 2023. Summary: This study is designed to study the effect of carbide forming elements such as V, Nb and Cr on the characteristic properties of S5 tool steel. In this work, five heats were prepared with different contents of carbide forming elements via vacuum meting and the effect of heat treatment (hardening, tempering and deep cryogenic treatment at - 196℃) of different steels on mechanical properties was investigated. The results of microscopic examination ,showed that the basic structure for the tested samples are tempered martensite for traditional S5 samples and fine tempered martensite for other micro alloyed samples. Wear rate also investigated by using pin on disc test at different loads 50 N and 100N with identification of friction coefficient through wear test.Scanning electron microscope was used to study the worn surfaces of the tested samples.Summary: تم تصميم هذه الدراسة لدراسة تأثير عناصر تشكيل الكربيد المختلفة مثل الفاناديوم والنيوبيوم والكروم على الخواص الميكانيكية لصلب العدة S5. في هذا العمل، تم تحضير خمس عينات بمحتويات مختلفة من عناصر تكوين الكربيد وتم فحص تأثير المعالجة الحرارية (التصلب والاعتدال والمعالجة التبريدية باستخدام النيتروجين المسال عند درجة حرارة - 196 درجة مئوية) على الخصائص الميكانيكية. تم حساب الأوستنيت المحتفظ به للعينات بواسطة طريقة حيود الأشعة السينية، كما تم استخدام اختبار الصدم لتحديد صلابة جميع العينات بعد ظروف المعالجة الحرارية المختلفة. أظهرت نتائج الفحص المجهري أن البنية الاساسية للعينات المختبرة عبارة عن مارتنسيت مخفف لعينات S5 التقليدية ومارتنسيت دقيق التركيب للعينات الاخرى من السبائك الدقيقة

Tags from this library: No tags from this library for this title. Log in to add tags.

Average rating: 0.0 (0 votes)

Holdings
Item type	Current library	Home library	Call number	Status	Barcode
Thesis	قاعة الرسائل الجامعية - الدور الاول	المكتبة المركزبة الجديدة - جامعة القاهرة	Cai01.13.13.Ph.D.2023.Ma.E. (Browse shelf(Opens below))	Not for loan	01010110089487000

Thesis (Ph.D)-Cairo University, 2023.

Bibliography: pages 200-250.

This study is designed to study the effect of carbide forming elements such as V,
Nb and Cr on the characteristic properties of S5 tool steel. In this work, five heats
were prepared with different contents of carbide forming elements via vacuum
meting and the effect of heat treatment (hardening, tempering and deep cryogenic
treatment at - 196℃) of different steels on mechanical properties was
investigated. The results of microscopic examination ,showed that the basic
structure for the tested samples are tempered martensite for traditional S5 samples
and fine tempered martensite for other micro alloyed samples. Wear rate also
investigated by using pin on disc test at different loads 50 N and 100N with
identification of friction coefficient through wear test.Scanning electron
microscope was used to study the worn surfaces of the tested samples.

تم تصميم هذه الدراسة لدراسة تأثير عناصر تشكيل الكربيد المختلفة مثل الفاناديوم والنيوبيوم والكروم على الخواص الميكانيكية لصلب العدة S5. في هذا العمل، تم تحضير خمس عينات بمحتويات مختلفة من عناصر تكوين الكربيد وتم فحص تأثير المعالجة الحرارية (التصلب والاعتدال والمعالجة التبريدية باستخدام النيتروجين المسال عند درجة حرارة - 196 درجة مئوية) على الخصائص الميكانيكية. تم حساب الأوستنيت المحتفظ به للعينات بواسطة طريقة حيود الأشعة السينية، كما تم استخدام اختبار الصدم لتحديد صلابة جميع العينات بعد ظروف المعالجة الحرارية المختلفة. أظهرت نتائج الفحص المجهري أن البنية الاساسية للعينات المختبرة عبارة عن مارتنسيت مخفف لعينات S5 التقليدية ومارتنسيت دقيق التركيب للعينات الاخرى من السبائك الدقيقة

Issued also as CD

Text in English and abstract in Arabic & English.

There are no comments on this title.

to post a comment.

Click on an image to view it in the image viewer