A study on the effect of alloying additions and heat treatment on the microstructure and properties of hyper - eutectoid (1.6in hundredcarbon) cast steel / Waleed Saied Elghazaly ; Supervised Yehia Salama Shash , Ragai Mohamed Rashad , Amer Eid Ali Amer

By:

Waleed Saied Elghazaly

Contributor(s):

Language: Eng Publication details: Cairo : Waleed Saied Elghazaly , 2006Description: 50P : ill ; 30cmOther title:

دراسة تاثير العناصر التسابكية والمعالجه الحراريه على البنية الميكروسكوبية والخواص الميكانيكية لمسبوك صلب هايبريوتكتويدى (1.6in hundred كربون) [Added title page title]

Subject(s):

Online resources:

Click here to access online

Available additional physical forms:

Issued also as CD

Dissertation note: Thesis (M.Sc.) - Cairo University - Faculty Of Engineering - Department Of Mechanical Design and Production Summary: The main goal for this investigation is to study and develop a new medium alloy austenitic structural steel that resembles austenitic stainless steels in room - temperature microstructure and some physical properties and can be used in some similar applicationsThe study comprises a series ofpearlitic hyper eutectoid cast steels of main analysis : 16 - 17 Carbonin hundred , 03 Silicon in hundred , 07 - 24 Manganese in hundred and 02 - 28 Chromium in hundredVanadium was added for refining the grains of the final steel matricesAfter melting and casting the steels were subjected to spherodizing annealing at 790 - 820?C to attain good machinability for preparing the preparation of the test specimens (tensile , hardness , dilatometry and microstructures)

Tags from this library: No tags from this library for this title. Log in to add tags.

Average rating: 0.0 (0 votes)

Holdings
Item type	Current library	Home library	Call number	Status	Barcode
Thesis	قاعة الرسائل الجامعية - الدور الاول	المكتبة المركزبة الجديدة - جامعة القاهرة	Cai01.13.13.M.Sc.2006.Wa.S. (Browse shelf(Opens below))	Not for loan	01010110046227000
CD - Rom	مخـــزن الرســائل الجـــامعية - البدروم	المكتبة المركزبة الجديدة - جامعة القاهرة	Cai01.13.13.M.Sc.2006.Wa.S. (Browse shelf(Opens below))	Not for loan	01020110046227000

Browsing المكتبة المركزبة الجديدة - جامعة القاهرة shelves Close shelf browser (Hides shelf browser)

Previous	No cover image available	No cover image available	No cover image available	No cover image available	No cover image available	No cover image available	No cover image available	Next
Previous	Cai01.13.13.M.Sc.2006.Wa.O The Optimization of the reels cutting planning problems using grouping genetic algorithms /	Cai01.13.13.M.Sc.2006.Wa.O The Optimization of the reels cutting planning problems using grouping genetic algorithms /	Cai01.13.13.M.Sc.2006.Wa.S. A study on the effect of alloying additions and heat treatment on the microstructure and properties of hyper - eutectoid (1.6in hundredcarbon) cast steel /	Cai01.13.13.M.Sc.2006.Wa.S. A study on the effect of alloying additions and heat treatment on the microstructure and properties of hyper - eutectoid (1.6in hundredcarbon) cast steel /	Cai01.13.13.M.Sc.2007.Ah.A Analysis of plastic shaping of a round tube into a square tubular section /	Cai01.13.13.M.Sc.2007.Ah.A Analysis of plastic shaping of a round tube into a square tubular section /	Cai01.13.13.M.Sc.2007.Ah.E Effect of processing parameters on the mechanical characteristics of nano - structured A356 / (AI2O3) P cast metal matrix composites (MMNCs) by RHEO - casting techniques /	Next

Thesis (M.Sc.) - Cairo University - Faculty Of Engineering - Department Of Mechanical Design and Production

The main goal for this investigation is to study and develop a new medium alloy austenitic structural steel that resembles austenitic stainless steels in room - temperature microstructure and some physical properties and can be used in some similar applicationsThe study comprises a series ofpearlitic hyper eutectoid cast steels of main analysis : 16 - 17 Carbonin hundred , 03 Silicon in hundred , 07 - 24 Manganese in hundred and 02 - 28 Chromium in hundredVanadium was added for refining the grains of the final steel matricesAfter melting and casting the steels were subjected to spherodizing annealing at 790 - 820?C to attain good machinability for preparing the preparation of the test specimens (tensile , hardness , dilatometry and microstructures)

Issued also as CD