Development of ceramic membranes structure for well water treatment / by Amira Mohamed Gaber Kasem ; Supervisors Prof. Magdi Fouad Abadir, Prof. Shakinaz Ali El-Sherbiny, Prof. Shereen Kamel Amin Kamel.

By:

Amira Mohamed Gaber Kasem [preparation.]

Contributor(s):

Material type:

TextLanguage: English Summary language: English, Arabic Producer: 2024Description: 87 pages : illustrations ; 30 cm. + CDContent type:

text

Media type:

Unmediated

Carrier type:

volume

Other title:

تطوير أغشية سيراميكية لمعالجة مياه الآبار [Added title page title]

Subject(s):

DDC classification:

628.114

Available additional physical forms:

Issues also as CD.

Dissertation note: Thesis (M.Sc)-Cairo University, 2024. Summary: Two types of clays were used; Aswan and Kaolin clays, Corn Starch as a pore-forming agent, and Polyvinyl Alcohol (PVA) as a binder material to fabricate ceramic membranes. The raw materials were characterized by XRF for chemical composition, XRD for mineralogical composition, DTA, and TGA for thermal analysis, and particle-size distribution. Ceramic membrane samples were prepared by uniaxial pressing method and pressed under a pressure of 10 MPa. Membrane samples were then dried, and fired at temperatures of 900, 1000, 1100, and 1200 °C. Then characterized by the determination of water absorption, bulk density, porosity, and compressive strength. The effect of temperature and the addition of starch by 5% on the permeate flux and salt rejection were assessed. The recommended membrane is found to be the one made from Kaolin clay without starch, and fired at 1000°C (KII). The selective layer of KII is developed by polymer layer deposition of cellulose acetate and then annealed at 60°C for 5 minutes. The polymer-ceramic membrane without annealing (P-CM1) achieved the highest salt rejection for well water treatmentSummary: تم استخدام نوعين من الطفلة هما الطفلة الأسواني والكاولين، ونشا الذرة كعامل تشكيل للمسام، وكحول البولي فينيل كمادة رابطة لتصنيع الأغشية السيراميكية. تم تشخيص المواد الخام باستخدام الفحص بأشعة حيود التوهج للتركيب الكيميائي وأشعة الحيود السينية لتركيب الأطوار والتحليل الحراري لتتبع التصرف عند الحريق وتحليل المناخل لمعرفة توزيع المقاس الحبيبي. تم تحضير محلول 3% من الكحول وخلطه مع كل نوع من نوعي الطفلة وتم الصب في قوالب اسطوانية تحت ضغط 10 ميجا باسكال. تم بعد ذلك تجفيف عينات الأغشية، وحرقها عند درجات حرارة تتراوح من 900 إلى 1200 ْم. تم اختبار العينات من حيث امتصاص الماء والمسامية الظاهرية والكثافة الكلية ومقاومة التهشم. تم تقييم تأثير درجة الحرارة وإضافة النشا بنسبة 5% على تدفق المياه وفصل الأملاح. تم بعد ذلك ترسيب طبقة بوليمرية من أسيتات السليولوز ومعالجتها حرارياً عند 60 ْم لمدة خمس دقائق. حقق غشاء البوليمر والسيراميك بدون المعالجة أعلى نسبة فصل للأملاح لمعالجة مياه الآبار.

Tags from this library: No tags from this library for this title. Log in to add tags.

Average rating: 0.0 (0 votes)

Holdings
Item type	Current library	Home library	Call number	Status	Barcode
Thesis	قاعة الرسائل الجامعية - الدور الاول	المكتبة المركزبة الجديدة - جامعة القاهرة	Cai01.13.04.M.Sc.2024.Am.D (Browse shelf(Opens below))	Not for loan	01010110090889000

Thesis (M.Sc)-Cairo University, 2024.

Bibliography: pages 82-87.

Two types of clays were used; Aswan and Kaolin clays, Corn Starch as a pore-forming agent, and Polyvinyl Alcohol (PVA) as a binder material to fabricate ceramic membranes. The raw materials were characterized by XRF for chemical composition, XRD for mineralogical composition, DTA, and TGA for thermal analysis, and particle-size distribution. Ceramic membrane samples were prepared by uniaxial pressing method and pressed under a pressure of 10 MPa. Membrane samples were then dried, and fired at temperatures of 900, 1000, 1100, and 1200 °C. Then characterized by the determination of water absorption, bulk density, porosity, and compressive strength. The effect of temperature and the addition of starch by 5% on the permeate flux and salt rejection were assessed. The recommended membrane is found to be the one made from Kaolin clay without starch, and fired at 1000°C (KII). The selective layer of KII is developed by polymer layer deposition of cellulose acetate and then annealed at 60°C for 5 minutes. The polymer-ceramic membrane without annealing (P-CM1) achieved the highest salt rejection for well water treatment

تم استخدام نوعين من الطفلة هما الطفلة الأسواني والكاولين، ونشا الذرة كعامل تشكيل للمسام، وكحول البولي فينيل كمادة رابطة لتصنيع الأغشية السيراميكية. تم تشخيص المواد الخام باستخدام الفحص بأشعة حيود التوهج للتركيب الكيميائي وأشعة الحيود السينية لتركيب الأطوار والتحليل الحراري لتتبع التصرف عند الحريق وتحليل المناخل لمعرفة توزيع المقاس الحبيبي. تم تحضير محلول 3% من الكحول وخلطه مع كل نوع من نوعي الطفلة وتم الصب في قوالب اسطوانية تحت ضغط 10 ميجا باسكال. تم بعد ذلك تجفيف عينات الأغشية، وحرقها عند درجات حرارة تتراوح من 900 إلى 1200 ْم. تم اختبار العينات من حيث امتصاص الماء والمسامية الظاهرية والكثافة الكلية ومقاومة التهشم. تم تقييم تأثير درجة الحرارة وإضافة النشا بنسبة 5% على تدفق المياه وفصل الأملاح. تم بعد ذلك ترسيب طبقة بوليمرية من أسيتات السليولوز ومعالجتها حرارياً عند 60 ْم لمدة خمس دقائق. حقق غشاء البوليمر والسيراميك بدون المعالجة أعلى نسبة فصل للأملاح لمعالجة مياه الآبار.

Issues also as CD.

Text in English and abstract in Arabic & English.

There are no comments on this title.

to post a comment.

جامعة القاهرة

المكتبة المركزية الجديدة

مكتبة جامعة القاهرة الأهلية

Development of ceramic membranes structure for well water treatment / by Amira Mohamed Gaber Kasem ; Supervisors Prof. Magdi Fouad Abadir, Prof. Shakinaz Ali El-Sherbiny, Prof. Shereen Kamel Amin Kamel.