Punching shear behavior of ferrocement panels exposed to elevated temperature /
Ahmed Mohamed Saad
Punching shear behavior of ferrocement panels exposed to elevated temperature / سلوك القص الثاقب لبلاطات الفيروسمنت المعرضة لدرجات الحرارة العالية Ahmed Mohamed Saad ; Supervised Hamed Mohamed Mahmoud , Ghada Diaa - Cairo : Ahmed Mohamed Saad , 2015 - 135 P. : charts , facsimiles ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Civil Engineering
The aim of this study is to investigate the behavior of ferrocement slabs exposure to elevated temperature under punching. Ten slab column connections were tested; the specimens have been divided into five groups. The test variables were the opening meshes size, diameter of meshes bars, elevated temperature exposure and fighting procedure. It is found that using ferrocement meshes instead of steel improve the punching shear resistance and the best design of ferrocement against fire consist of 10 layers with opening size 70x70 mm and 4 mm diameter
Ductility Ferrocement Punching
Punching shear behavior of ferrocement panels exposed to elevated temperature / سلوك القص الثاقب لبلاطات الفيروسمنت المعرضة لدرجات الحرارة العالية Ahmed Mohamed Saad ; Supervised Hamed Mohamed Mahmoud , Ghada Diaa - Cairo : Ahmed Mohamed Saad , 2015 - 135 P. : charts , facsimiles ; 30cm
Thesis (M.Sc.) - Cairo University - Faculty of Engineering - Department of Civil Engineering
The aim of this study is to investigate the behavior of ferrocement slabs exposure to elevated temperature under punching. Ten slab column connections were tested; the specimens have been divided into five groups. The test variables were the opening meshes size, diameter of meshes bars, elevated temperature exposure and fighting procedure. It is found that using ferrocement meshes instead of steel improve the punching shear resistance and the best design of ferrocement against fire consist of 10 layers with opening size 70x70 mm and 4 mm diameter
Ductility Ferrocement Punching